Strontium Ferrite Disc Magnet: Presintered at 1100 °C, 0.2 mol SrCO3 to 1.1 mol Iron Oxide (Went, Philips 1956, Ex. 7)
A strontium ferrite: 0.2 mol strontium carbonate to 1.1 mol iron oxide, dried, milled, presintered 3.5 hours at 1100 °C, bound, formed and passed through a 1280 °C furnace in 10 minutes. Went's rod held 2,155 gauss with a coercive force of 2,500 oersted.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 7. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
고급
2 days
안내
1
1
Weigh strontium carbonate and iron oxide
Weigh strontium carbonate and iron oxide
Weigh 29.5 g strontium carbonate (0.2 mol) and 176.1 g ferric oxide (1.1 mol).
이 단계의 재료:
탄산스트론튬29.5 g
산화제이철176.1 g필요한 도구:
접시 저울
P100 방진 마스크2
2
Dry at 200 °C, mill with alcohol 4 hours
Dry at 200 °C, mill with alcohol 4 hours
Dry the mixture at 200 °C, then grind it with alcohol in a ball mill for 4 hours and dry it.
필요한 도구:
건조 가마
철 볼 밀
에탄올 - 실험실 등급, 95 %3
3
Presinter in air at 1100 °C for 3.5 hours
Presinter in air at 1100 °C for 3.5 hours
Fire the powder in air at 1100 °C for about 3.5 hours.
필요한 도구:
머플로
뚜껑 달린 도가니(자기)
도가니 집게
내열 장갑4
4
Add a binder and form, dry overnight
Add a binder and form, dry overnight
Add a binder as in Example 1 (polyvinyl alcohol or nitrocellulose). The patent extrudes rods; ours: press discs at 1.5 tonnes per cm². Dry overnight.
필요한 도구:
폴리비닐알코올 분말
유압 프레스
원판 압축 금형건조 가마5
5
Pass through a 1280 °C zone in 10 minutes
Pass through a 1280 °C zone in 10 minutes
Sinter in air at 1280 °C by passing the pieces through a 10 cm hot zone at 10 mm per minute: 10 minutes in the heat.
필요한 도구:
관상로내열 장갑6
6
Magnetise the discs
Magnetise the discs
The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.
필요한 도구:
전자석
나침반이 블루프린트로 만드는 것
관련 블루프린트
이 블루프린트들은 지식을 공유합니다 — 기술, 재료 또는 원리
CC0 퍼블릭 도메인
이 블루프린트는 CC0로 공개되었습니다. 어떤 목적으로든 자유롭게 복사, 수정, 배포 및 사용할 수 있습니다.
제품 구매를 통해 메이커를 지원하세요. 판매자가 설정한 메이커 커미션 을 받거나, 이 블루프린트의 새로운 반복을 만들어 연결로 포함시킬 수 있습니다.