Oriented Strontium Ferrite Disc Magnet: Agate-Milled, 10,000 Oersted Field (Gorter, Philips 1956, Ex. 8)
A strontium ferrite magnet oriented in a magnetic field: strontium carbonate and iron oxide milled, pre-fired 2 hours at 1000 °C, ground fine in an agate mill, then oriented, heated and sintered as in Example 4. In the principal direction it held 2,640 gauss with a coercive force of 2,825 oersted and a (BH)max of 1.63 × 10⁶.
Source: E. W. Gorter, G. W. Rathenau and A. L. Stuyts (Philips), US 2,762,778 (1956), Example 8. They made blocks; disc size is ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Ilọsíwájú
3 days
Ìlànà
1
1
Weigh strontium carbonate and iron oxide
Weigh strontium carbonate and iron oxide
Weigh 29.5 g strontium carbonate and 179 g ferric oxide.
Àwọn ohun èlò fún ìgbésẹ̀ yìí:
Strontium carbonate29.5 g
Ọ́kísáìdì irin (III)179 gÀwọn irinṣẹ́ tí a nílò:
Òǹwọ̀n ìdọ́gba
Ẹ̀rọ Ìmí P1002
2
Mill 15 hours with alcohol, dry
Mill 15 hours with alcohol, dry
Grind in a ball mill with alcohol for 15 hours. Remove the alcohol and dry the powder.
Àwọn irinṣẹ́ tí a nílò:
Ẹ̀rọ Lílọ Bọ́ọ̀lù Irin
Ethanol - ìpele ilé-ìwádìí, 95 %
Ààrò ìgbẹ̀3
3
Pre-fire 2 hours at 1000 °C in air
Pre-fire 2 hours at 1000 °C in air
Heat the powder for 2 hours at 1000 °C in an electric furnace in air. Let it cool.
Àwọn irinṣẹ́ tí a nílò:
Ààrò muffle
Ìkòkò ìyọ́ pẹ̀lú ìdérí (porcelain)
Ẹmú Ìkòkò Ìyọ́
Ìbọ̀wọ́ Tí Ń Fara Da Ooru4
4
Grind 4 hours in an agate centrifugal mill
Grind 4 hours in an agate centrifugal mill
Grind the cooled material for 4 hours with alcohol in an agate centrifugal mill, then dry it. This is the pre-fired powder.
Àwọn irinṣẹ́ tí a nílò:
Ẹ̀rọ ìlọ̀ yíyí ti òkúta àgéètìEthanol - ìpele ilé-ìwádìí, 95 %Ààrò ìgbẹ̀5
5
Stir into 8 % polyvinyl acetate in acetone
Stir into 8 % polyvinyl acetate in acetone
Dissolve polyvinyl acetate in acetone to a 8 % solution and stir the pre-fired powder into it, 1 cc of solution per gram of powder. The binder burns off later.
Àwọn irinṣẹ́ tí a nílò:
Polyvinyl acetate
AcetoneÒǹwọ̀n ìdọ́gba6
6
Orient in a 10000 oersted field
Orient in a 10000 oersted field
Put the suspension in a moulding die between the poles of a magnet and apply a first field of 10000 oersted. Remove the binder solution while the field is on.
Àwọn irinṣẹ́ tí a nílò:
Mọ́ọ̀dù títẹ díìsì
Òòfà iná-mànàmáná
Ẹ̀rọ ìtẹ̀ háídírọ́líìkì7
7
Heat to 500 °C in a 2000 oersted field
Heat to 500 °C in a 2000 oersted field
Put the block in an electric furnace between the magnet's poles. With a second field of 2000 oersted along the first field's direction, heat to 500 °C, which burns off the rest of the binder. Then switch the field off.
Àwọn irinṣẹ́ tí a nílò:
Ààrò Ọ̀pọ́nÒòfà iná-mànàmánáÌbọ̀wọ́ Tí Ń Fara Da Ooru8
8
Sinter: through a 1280 °C zone in 5 minutes
Sinter: through a 1280 °C zone in 5 minutes
Pass the block at 20 mm per minute through an electric furnace in air at 1280 °C with a 10 cm hot zone: about 5 minutes in the heat.
Àwọn irinṣẹ́ tí a nílò:
Ààrò Ọ̀pọ́nÌbọ̀wọ́ Tí Ń Fara Da Ooru9
9
Magnetise in the principal direction
Magnetise in the principal direction
Magnetise the block along the direction of the first field, the principal direction. The patent magnetises it in a field in that direction; ours: an electromagnet. Find the north face with a compass.
Àwọn irinṣẹ́ tí a nílò:
Òòfà iná-mànàmáná
Kọ́mpasiÀwọn ohun-èlò
2- 29.5 gÀyè
- 179 gÀyè
Àwọn irinṣẹ́ tó nílò
17- Àyè
- Àyè
- Àyè
- Àyè
- Àyè
Ìtọ́nisọ́nà yìí ń ṣe
Blueprint tó jọra
Àwọn blueprint wọ̀nyí pín ìmọ̀ — ọ̀nà, ohun-èlò tàbí ìlànà
CC0 Àgbègbè Gbogbogbò
Blueprint yìí ti jáde lábẹ́ CC0. O lè ṣe àdàkọ, yí padà, pín, àti lò láìsí ìyọ̀ǹda.
Ṣàtìlẹ́yìn Olùṣẹ́dá nípa rírà àwọn ọjà nipasẹ̀ Blueprint wọn Ẹ̀san Olùṣẹ́dá tí àwọn Olùtajà gbé kalẹ̀, tàbí ṣẹ̀dá àtúnṣe tuntun ti Blueprint yìí kí o sì fi sínú Blueprint rẹ gẹ́gẹ́ bí ìsopọ̀ láti pín owó-wíwọlé.