Strontium-Calcium Ferrite Disc Magnet: 0.08 mol SrCO3 and 0.02 mol CaCO3, 1280 °C (Went, Philips 1956, Ex. 23)
A strontium ferrite with a fifth of the strontium replaced by calcium: 0.08 mol strontium carbonate and 0.02 mol calcium carbonate to 0.6 mol iron oxide, ground, dried, formed and passed through a 1280 °C furnace in 10 minutes. Went's rod held 2,320 gauss with a coercive force of 1,395 oersted.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 23. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Ilọsíwájú
2 days
Ìlànà
1
1
Weigh the carbonates and iron oxide
Weigh the carbonates and iron oxide
Weigh 11.81 g strontium carbonate (0.08 mol), 2.002 g calcium carbonate (0.02 mol), 95.55 g ferric oxide (0.6 mol).
Àwọn ohun èlò fún ìgbésẹ̀ yìí:
Strontium carbonate11.81 g
Calcium carbonate (ẹfun funfun)2.002 g
Ọ́kísáìdì irin (III)95.55 gÀwọn irinṣẹ́ tí a nílò:
Òǹwọ̀n ìdọ́gba
Ẹ̀rọ Ìmí P1002
2
Mill with alcohol 4 hours, dry
Mill with alcohol 4 hours, dry
As in Examples 18 to 21: grind the mixture with alcohol in a ball mill for 4 hours, then dry it.
Àwọn irinṣẹ́ tí a nílò:
Ẹ̀rọ Lílọ Bọ́ọ̀lù Irin
Ethanol - ìpele ilé-ìwádìí, 95 %
Ààrò ìgbẹ̀3
3
Press at 1.5 t/cm²
Press at 1.5 t/cm²
Example 23 does not say whether the 1000 °C presinter of Examples 18 to 21 is used. Press the dry powder at 1.5 tonnes per cm² (ours: discs instead of a rod).
Àwọn irinṣẹ́ tí a nílò:
Ẹ̀rọ ìtẹ̀ háídírọ́líìkì
Mọ́ọ̀dù títẹ díìsì4
4
Pass through a 1280 °C zone in 10 minutes
Pass through a 1280 °C zone in 10 minutes
Sinter at 1280 °C by passing the pieces through a 10 cm hot zone at 10 mm per minute: 10 minutes in the heat.
Àwọn irinṣẹ́ tí a nílò:
Ààrò Ọ̀pọ́n
Ìbọ̀wọ́ Tí Ń Fara Da Ooru5
5
Magnetise the discs
Magnetise the discs
The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.
Àwọn irinṣẹ́ tí a nílò:
Òòfà iná-mànàmáná
Kọ́mpasiÀwọn ohun-èlò
3- 11.81 gÀyè
- Àyè
- 95.55 gÀyè
Àwọn irinṣẹ́ tó nílò
11- Àyè
- Àyè
- Àyè
Ìtọ́nisọ́nà yìí ń ṣe
Blueprint tó jọra
Àwọn blueprint wọ̀nyí pín ìmọ̀ — ọ̀nà, ohun-èlò tàbí ìlànà
CC0 Àgbègbè Gbogbogbò
Blueprint yìí ti jáde lábẹ́ CC0. O lè ṣe àdàkọ, yí padà, pín, àti lò láìsí ìyọ̀ǹda.
Ṣàtìlẹ́yìn Olùṣẹ́dá nípa rírà àwọn ọjà nipasẹ̀ Blueprint wọn Ẹ̀san Olùṣẹ́dá tí àwọn Olùtajà gbé kalẹ̀, tàbí ṣẹ̀dá àtúnṣe tuntun ti Blueprint yìí kí o sì fi sínú Blueprint rẹ gẹ́gẹ́ bí ìsopọ̀ láti pín owó-wíwọlé.