Strontium Ferrite Disc Magnet: 1 : 10 Strontium to Iron Oxide, 1280 °C (Went, Philips 1956, Ex. 26)
A strontium ferrite with much more iron oxide: 0.1 mol strontium carbonate to 1 mol, made as in Example 25 but passed through a 1280 °C furnace in 10 minutes. Went's rod held 1,200 gauss with a coercive force of 3,610 oersted.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 26. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Ilọsíwájú
2 days
Ìlànà
1
1
Weigh strontium carbonate and iron oxide
Weigh strontium carbonate and iron oxide
Weigh 14.76 g strontium carbonate (0.1 mol) and 159.7 g ferric oxide (1 mol).
Àwọn ohun èlò fún ìgbésẹ̀ yìí:
Strontium carbonate14.76 g
Ọ́kísáìdì irin (III)159.7 gÀwọn irinṣẹ́ tí a nílò:
Òǹwọ̀n ìdọ́gba
Ẹ̀rọ Ìmí P1002
2
Mill, presinter and mill as in Example 25
Mill, presinter and mill as in Example 25
As in Example 25: grind with alcohol 7 hours, dry at 110 °C, fire in air at 1000 °C for 4 hours, grind again and dry.
Àwọn irinṣẹ́ tí a nílò:
Ẹ̀rọ Lílọ Bọ́ọ̀lù Irin
Ethanol - ìpele ilé-ìwádìí, 95 %
Ààrò ìgbẹ̀
Ààrò muffle
Ìkòkò ìyọ́ pẹ̀lú ìdérí (porcelain)
Ẹmú Ìkòkò Ìyọ́3
3
Press at 1.5 t/cm²
Press at 1.5 t/cm²
Press at 1.5 tonnes per cm² (ours: discs).
Àwọn irinṣẹ́ tí a nílò:
Ẹ̀rọ ìtẹ̀ háídírọ́líìkì
Mọ́ọ̀dù títẹ díìsì4
4
Pass through a 1280 °C zone in 10 minutes
Pass through a 1280 °C zone in 10 minutes
Sinter at 1280 °C by passing the pieces through a 10 cm hot zone at 10 mm per minute: 10 minutes in the heat.
Àwọn irinṣẹ́ tí a nílò:
Ààrò Ọ̀pọ́n
Ìbọ̀wọ́ Tí Ń Fara Da Ooru5
5
Magnetise the discs
Magnetise the discs
The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.
Àwọn irinṣẹ́ tí a nílò:
Òòfà iná-mànàmáná
Kọ́mpasiÀwọn ohun-èlò
2- 14.76 gÀyè
- 159.7 gÀyè
Àwọn irinṣẹ́ tó nílò
14- Àyè
- Àyè
- Àyè
- Àyè
Ìtọ́nisọ́nà yìí ń ṣe
Blueprint tó jọra
Àwọn blueprint wọ̀nyí pín ìmọ̀ — ọ̀nà, ohun-èlò tàbí ìlànà
CC0 Àgbègbè Gbogbogbò
Blueprint yìí ti jáde lábẹ́ CC0. O lè ṣe àdàkọ, yí padà, pín, àti lò láìsí ìyọ̀ǹda.
Ṣàtìlẹ́yìn Olùṣẹ́dá nípa rírà àwọn ọjà nipasẹ̀ Blueprint wọn Ẹ̀san Olùṣẹ́dá tí àwọn Olùtajà gbé kalẹ̀, tàbí ṣẹ̀dá àtúnṣe tuntun ti Blueprint yìí kí o sì fi sínú Blueprint rẹ gẹ́gẹ́ bí ìsopọ̀ láti pín owó-wíwọlé.