Strontium Ferrite Disc Magnet: 1 mol SrCO3 to 2.5 mol Iron Oxide, 1200 °C (Went, Philips 1956, Ex. 9)
A strontium ferrite: 1 mol strontium carbonate to 2.5 mol iron oxide, milled, bound and formed as in Example 4, and passed through a 1200 °C furnace in 3 to 5 minutes. Went's rod held 1,555 gauss with a coercive force of 3,160 oersted.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 9. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Ilọsíwájú
2 days
Ìlànà
1
1
Weigh strontium carbonate and iron oxide
Weigh strontium carbonate and iron oxide
Weigh 147.6 g strontium carbonate (1 mol) and 403.4 g ferric oxide (2.5 mol).
Àwọn ohun èlò fún ìgbésẹ̀ yìí:
Strontium carbonate147.6 g
Ọ́kísáìdì irin (III)403.4 gÀwọn irinṣẹ́ tí a nílò:
Òǹwọ̀n ìdọ́gba
Ẹ̀rọ Ìmí P1002
2
Mill with alcohol 15.5 hours, dry and sieve
Mill with alcohol 15.5 hours, dry and sieve
As in Example 4: grind the mixture with alcohol in a ball mill for 15.5 hours, then dry it and sieve it.
Àwọn irinṣẹ́ tí a nílò:
Ẹ̀rọ Lílọ Bọ́ọ̀lù Irin
Ethanol - ìpele ilé-ìwádìí, 95 %
Ààrò ìgbẹ̀
Ajọ̀3
3
Knead with a binder and form
Knead with a binder and form
Mix 300 g of the powder with a binder such as polyvinyl alcohol (Went names it or nitrocellulose) into a kneadable mass. The patent extrudes rods about 3 mm across; ours: press discs at 1.5 tonnes per cm², as in its other examples. Dry them in air for about 24 hours.
Àwọn irinṣẹ́ tí a nílò:
Ẹ̀lúbọ́ polyvinyl alcohol
Ẹ̀rọ ìtẹ̀ háídírọ́líìkì
Mọ́ọ̀dù títẹ díìsìÀàrò ìgbẹ̀4
4
Pass through a 1200 °C zone in 3 to 5 minutes
Pass through a 1200 °C zone in 3 to 5 minutes
Sinter in air at 1200 °C by passing the pieces through a 3 to 5 cm hot zone at 10 mm per minute: 3 to 5 minutes in the heat.
Àwọn irinṣẹ́ tí a nílò:
Ààrò Ọ̀pọ́n
Ìbọ̀wọ́ Tí Ń Fara Da Ooru5
5
Magnetise the discs
Magnetise the discs
The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.
Àwọn irinṣẹ́ tí a nílò:
Òòfà iná-mànàmáná
Kọ́mpasiÀwọn ohun-èlò
2- 147.6 gÀyè
- 403.4 gÀyè
Àwọn irinṣẹ́ tó nílò
13- Àyè
- Àyè
- Àyè
- Àyè
Ìtọ́nisọ́nà yìí ń ṣe
Blueprint tó jọra
Àwọn blueprint wọ̀nyí pín ìmọ̀ — ọ̀nà, ohun-èlò tàbí ìlànà
CC0 Àgbègbè Gbogbogbò
Blueprint yìí ti jáde lábẹ́ CC0. O lè ṣe àdàkọ, yí padà, pín, àti lò láìsí ìyọ̀ǹda.
Ṣàtìlẹ́yìn Olùṣẹ́dá nípa rírà àwọn ọjà nipasẹ̀ Blueprint wọn Ẹ̀san Olùṣẹ́dá tí àwọn Olùtajà gbé kalẹ̀, tàbí ṣẹ̀dá àtúnṣe tuntun ti Blueprint yìí kí o sì fi sínú Blueprint rẹ gẹ́gẹ́ bí ìsopọ̀ láti pín owó-wíwọlé.