Bearing Steel Bar (52100): Crucible Steel Alloyed with Chromium
52100 is the steel of ball bearings: about 1 % carbon and 1.5 % chromium (ASM). The standard, ASTM A295, allows 0.93–1.05 % carbon and 1.35–1.60 % chromium. Here crucible steel is melted with chromium and a little manganese, cast, forged to bar and annealed soft for working.
Our method, not the factory one: factory 52100 is melted in an electric furnace and vacuum-degassed to meet the standard's limits on inclusions. A crucible melt can reach the composition, but only a lab test shows whether it is clean enough for bearings.
The picture: our drawing, crucible to bar.
उन्नत
2 days
निर्देशनहरू
1
1
Weigh the charge
Weigh the charge
For 1 kg: 981.5 g crucible steel of about 1 % carbon, 15 g chromium and 3.5 g manganese (our figures; see the last step). Use steel whose analysis you know.
यस चरणका सामग्री:
मुसा इस्पात981.5 ग्राम
क्रोमियम धातु15 ग्राम
म्याङ्गनिज3.5 ग्रामचाहिने औजार:
डिजिटल भान्साको तराजु2
2
Melt
Melt
Pack the steel, chromium and manganese in a covered clay crucible and melt it in the furnace. The alloy is fully liquid above 1450 °C.
चाहिने औजार:
गहिरो माटोको मुसा
इँटाको भट्टी
खलाती
वेल्डिङका पन्जा
छालाको एप्रन
सुरक्षा चस्मा3
3
Cast the ingot
Cast the ingot
Lift the crucible out with tongs and pour into a cast-iron ingot mould. Let it cool.
चाहिने औजार:
मुसाको चिम्टा
पिण्डको साँचोवेल्डिङका पन्जाछालाको एप्रनसुरक्षा चस्मा4
4
Forge to bar
Forge to bar
Heat the ingot to a cherry-red heat and no hotter, and draw it out on the anvil to a round or square bar. Reheat when the colour drops; never hammer it cold.
यस चरणका सामग्री:
कोइला1 as requiredचाहिने औजार:
आरनको भट्टी
निहुँ
घन
तेर्सो फन्को भएको हथौडा
आरनको सँड़सी
डिजिटल क्यालिपर ६ इन्चवेल्डिङका पन्जाछालाको एप्रनसुरक्षा चस्मा5
5
Test the analysis
Test the analysis
Drill clean chips from the bar and have a lab analyse carbon, chromium, manganese, silicon, phosphorus and sulphur. Keep the bar only if it is within 52100 limits.
चाहिने औजार:
हाते ड्रिल
बिर्को भएको सिसाको भाँडोसुरक्षा चस्मा6
6
Anneal soft
Anneal soft
In the oven, hold the bar at 793 °C (1460 °F) for 30 minutes, cool in the oven no faster than 500 °C an hour to 682 °C (1260 °F), then cool in air (Verhoeven's anneal).
चाहिने औजार:
तातो उपचार भट्टी
पढाइसहितको तापयुग्मआरनको सँड़सीवेल्डिङका पन्जा7
7
The charge
The charge
Jupyter नोटबुक लोड हुँदैछ…
सामग्री
4- 981.5 ग्रामप्लेसहोल्डर
- 15 ग्रामप्लेसहोल्डर
- 3.5 ग्रामप्लेसहोल्डर
- 1 as requiredप्लेसहोल्डर
आवश्यक उपकरणहरू
19- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
यो खाकाले बनाउँछ
सम्बन्धित ब्लुप्रिन्ट
यी ब्लुप्रिन्टहरूले ज्ञान साझा गर्छन् — प्रविधि, सामग्री वा सिद्धान्त
CC0 सार्वजनिक डोमेन
यो ब्लुप्रिन्ट CC0 अन्तर्गत जारी गरिएको छ। तपाईं अनुमति नसोधी प्रतिलिपि, परिमार्जन, वितरण र प्रयोग गर्न सक्नुहुन्छ।
ब्लुप्रिन्ट मार्फत उत्पादनहरू किनेर सिर्जनाकर्तालाई सहयोग गर्नुहोस् सिर्जनाकर्ता कमिसन विक्रेताले तोकेको, वा यो ब्लुप्रिन्टको नयाँ संस्करण बनाउनुहोस् र आम्दानी बाँड्न आफ्नो ब्लुप्रिन्टमा जडानको रूपमा समावेश गर्नुहोस्।