Ferrite Toroid Core: Copper-Zinc Ferrite Sintered at 1100 °C, Presintered Twice at 900 °C (Snoek 1948, Ex. I)
A soft ferrite ring core for coils and transformers: copper, zinc and iron oxides with a little brownstone, presintered twice at 900 °C, pressed into a ring and sintered at 1100 °C in oxygen. Snoek's ring had an initial permeability of 154.
Source: J. L. Snoek, US 2,452,530 (Philips, 1948), Example I and its table. Unknown: the 'violet' iron oxide, linked to an unknown head. Picture: the patent's Fig. 4, the ring core.
उन्नत
2 days
निर्देशनहरू
1
1
Weigh 20 : 30 : 50 mol % and 1 % brownstone
Weigh 20 : 30 : 50 mol % and 1 % brownstone
Mix 20 mol % pure copper oxide, 30 mol % pure zinc oxide and 50 mol % pure violet iron oxide, and add 1 % by weight of brownstone (manganese dioxide). Ours, by weight: 13.24 g copper oxide, 20.32 g zinc oxide and 66.44 g iron oxide per 100 g, plus 1 g brownstone. Unknown: what makes the iron oxide 'violet'; Snoek does not say.
यस चरणका सामग्री:
तामाको अक्साइड13.24 ग्राम
जिंक अक्साइड धुलो20.32 ग्राम
बैजनी आइरन अक्साइड66.44 ग्राम
म्याङ्गनिज डाइअक्साइड (पाइरोलुसाइट)1 ग्रामचाहिने औजार:
समभुज तराजु
धूलोको मास्क2
2
Grind half an hour in an iron ball mill
Grind half an hour in an iron ball mill
Grind the mixture for half an hour in a mill with iron balls.
चाहिने औजार:
फलामे बल मिलधूलोको मास्क3
3
Presinter at 900 °C for 2 hours in oxygen
Presinter at 900 °C for 2 hours in oxygen
Heat the ground powder to 900 °C for 2 hours in oxygen and let it cool.
चाहिने औजार:
ट्युब फर्नेस
अक्सिजन
चापयुक्त ग्यासको सिलिन्डर
पाइरोमिटर
बिर्कोसहितको क्रुसिबल (चिनियाँ माटो)
ताप सहने पन्जा4
4
Grind and presinter at 900 °C again (2 of 2)
Grind and presinter at 900 °C again (2 of 2)
Grind the powder, then heat it once more to 900 °C in oxygen. Snoek gives no times for the repeats.
चाहिने औजार:
फलामे बल मिलट्युब फर्नेसअक्सिजनचापयुक्त ग्यासको सिलिन्डरबिर्कोसहितको क्रुसिबल (चिनियाँ माटो)ताप सहने पन्जाधूलोको मास्क5
5
Grind 2 hours with iron balls
Grind 2 hours with iron balls
Grind it for 2 hours in a disintegrator with iron balls.
चाहिने औजार:
फलामे बल मिलधूलोको मास्क6
6
Press a ring at 4 tons per cm²
Press a ring at 4 tons per cm²
Press the powder at 4 tons per square centimetre into a ring 3 cm across with a 4 × 4 mm cross-section.
चाहिने औजार:
हाइड्रोलिक प्रेस
रिङ प्रेसिङ डाइधूलोको मास्क7
7
Sinter at 1100 °C in oxygen, cool 5–10 °C a minute
Sinter at 1100 °C in oxygen, cool 5–10 °C a minute
Sinter the ring at 1100 °C in a current of oxygen. Example I heats for 1 hour and cools in the oxygen at 5 to 10 °C per minute. Snoek's ring had an initial permeability of 154, measured at room temperature at 2 kHz.
चाहिने औजार:
ट्युब फर्नेसअक्सिजनचापयुक्त ग्यासको सिलिन्डरपाइरोमिटर
मुसाको चिम्टाताप सहने पन्जासामग्री
4- 13.24 ग्रामप्लेसहोल्डर
- 20.32 ग्रामप्लेसहोल्डर
- 66.44 ग्रामप्लेसहोल्डर
- प्लेसहोल्डर
आवश्यक उपकरणहरू
12- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
यो खाकाले बनाउँछ
सम्बन्धित ब्लुप्रिन्ट
यी ब्लुप्रिन्टहरूले ज्ञान साझा गर्छन् — प्रविधि, सामग्री वा सिद्धान्त
CC0 सार्वजनिक डोमेन
यो ब्लुप्रिन्ट CC0 अन्तर्गत जारी गरिएको छ। तपाईं अनुमति नसोधी प्रतिलिपि, परिमार्जन, वितरण र प्रयोग गर्न सक्नुहुन्छ।
ब्लुप्रिन्ट मार्फत उत्पादनहरू किनेर सिर्जनाकर्तालाई सहयोग गर्नुहोस् सिर्जनाकर्ता कमिसन विक्रेताले तोकेको, वा यो ब्लुप्रिन्टको नयाँ संस्करण बनाउनुहोस् र आम्दानी बाँड्न आफ्नो ब्लुप्रिन्टमा जडानको रूपमा समावेश गर्नुहोस्।