Ferrite Toroid Core: Copper-Zinc Ferrite by the Wet Process, Precipitated with Caustic Soda (Snoek 1948)
Snoek's copper-zinc ferrite made the wet way: copper, zinc and iron salts thrown down together with hot caustic soda, so the particles are very fine and pure. The washed deposit is pre-heated, pressed into a ring and fired in oxygen, with a 30-hour hold at 600 °C. His core reached an initial permeability of 500.
Source: J. L. Snoek, US 2,452,529 (Philips, 1948), Example II, wet process. Picture: our diagram.
उन्नत
3 days
निर्देशनहरू
1
1
Dissolve the copper, zinc and iron salts
Dissolve the copper, zinc and iron salts
Make 1 litre of a purified solution of 0.2 mol copper sulphate, 0.3 mol zinc sulphate and 1 mol iron nitrate. Ours: 49.94 g copper sulphate pentahydrate; weigh the zinc sulphate and ferric nitrate for the hydrate you have.
यस चरणका सामग्री:
कपर सल्फेट पञ्चहाइड्रेट (CuSO4·5H2O)49.94 ग्राम
जिङ्क सल्फेट0.3 mol
फेरिक नाइट्रेट1 mol
आसुत पानी1 lचाहिने औजार:
समभुज तराजु
बोरोसिलिकेट बिकर
रबरका पन्जा2
2
Precipitate hot with 9 M caustic soda
Precipitate hot with 9 M caustic soda
Heat the solution and precipitate it with 0.5 litre of 9 molar caustic soda. Ours: 180 g sodium hydroxide in water to 0.5 litre. Strong alkali: goggles and gloves.
यस चरणका सामग्री:
सोडियम हाइड्रोक्साइड — प्रयोगशाला स्तर180 ग्रामचाहिने औजार:
बोरोसिलिकेट बिकर
तताउने प्लेट
रासायनिक छिटाको चस्मारबरका पन्जा3
3
Wash, dry and pre-heat at 700 °C
Wash, dry and pre-heat at 700 °C
Wash out the deposit, dry it, and pre-heat it at 700 °C so it moulds better.
चाहिने औजार:
छान्ने कागजआसुत पानी
सुकाउने भट्टी
ट्युब फर्नेस
बिर्कोसहितको क्रुसिबल (चिनियाँ माटो)
ताप सहने पन्जा4
4
Mould a ring at 4 tons per cm²
Mould a ring at 4 tons per cm²
Mould the powder at 4 tons per square centimetre into a ring 3 cm across with a 4 × 4 mm section.
चाहिने औजार:
हाइड्रोलिक प्रेस
रिङ प्रेसिङ डाइ
धूलोको मास्क5
5
Heat 3 hours at 900 °C, cool to 600 °C, hold 30 hours
Heat 3 hours at 900 °C, cool to 600 °C, hold 30 hours
Heat the ring for about 3 hours at 900 °C, cool it to 600 °C at 5 °C per minute, hold it there for 30 hours and let it cool to room temperature, all in a current of oxygen. Snoek's core: initial permeability 500.
चाहिने औजार:
ट्युब फर्नेस
अक्सिजन
चापयुक्त ग्यासको सिलिन्डर
पाइरोमिटर
मुसाको चिम्टाताप सहने पन्जासामग्री
5- 49.94 ग्रामप्लेसहोल्डर
- 0.3 molप्लेसहोल्डर
- 1 molप्लेसहोल्डर
- 1 lप्लेसहोल्डर
- प्लेसहोल्डर
आवश्यक उपकरणहरू
18- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
यो खाकाले बनाउँछ
सम्बन्धित ब्लुप्रिन्ट
यी ब्लुप्रिन्टहरूले ज्ञान साझा गर्छन् — प्रविधि, सामग्री वा सिद्धान्त
CC0 सार्वजनिक डोमेन
यो ब्लुप्रिन्ट CC0 अन्तर्गत जारी गरिएको छ। तपाईं अनुमति नसोधी प्रतिलिपि, परिमार्जन, वितरण र प्रयोग गर्न सक्नुहुन्छ।
ब्लुप्रिन्ट मार्फत उत्पादनहरू किनेर सिर्जनाकर्तालाई सहयोग गर्नुहोस् सिर्जनाकर्ता कमिसन विक्रेताले तोकेको, वा यो ब्लुप्रिन्टको नयाँ संस्करण बनाउनुहोस् र आम्दानी बाँड्न आफ्नो ब्लुप्रिन्टमा जडानको रूपमा समावेश गर्नुहोस्।