High-Carbon Steel Wire Rod: Billet Hot-Rolled to 9 mm and Coiled
Wire is drawn from rod, and the rod is rolled hot. In a rod mill a steel billet is heated above its recrystallisation temperature and passed through stand after stand of grooved rolls, each one narrower, until it is a round rod about 9 mm thick. The rod is laid in a coil, ready to be cleaned and drawn into wire.
The picture: our diagram, square billet to round rod to coil.
उन्नत
Factory process
निर्देशनहरू
1
1
Heat the billet
Heat the billet
Heat the high-carbon billet above the steel's recrystallisation temperature.
यस चरणका सामग्री:
उच्च कार्बन फलामको बिलेट1 टुक्राचाहिने औजार:
इन्डक्सन हिटर2
2
Roll through the stands
Roll through the stands
Pass it through the roughing, intermediate and finishing stands of the rod mill. Each pair of grooved rolls makes the section smaller and rounder, down to about 9 mm.
चाहिने औजार:
बेल्ने मिल3
3
Keep it hot
Keep it hot
Finish about 50–100 °C above the recrystallisation temperature; reheat if the bar cools below it before the last passes.
चाहिने औजार:
इन्डक्सन हिटर4
4
Coil the rod
Coil the rod
Lay the hot rod in loops into a coil and let it cool. It comes out covered in mill scale, which is removed before drawing.
5
5
Rod length from one billet
Rod length from one billet
Jupyter नोटबुक लोड हुँदैछ…
सामग्री
1- 1 टुक्राप्लेसहोल्डर
आवश्यक उपकरणहरू
2- प्लेसहोल्डर
- प्लेसहोल्डर
यो खाकाले बनाउँछ
सम्बन्धित ब्लुप्रिन्ट
यी ब्लुप्रिन्टहरूले ज्ञान साझा गर्छन् — प्रविधि, सामग्री वा सिद्धान्त
CC0 सार्वजनिक डोमेन
यो ब्लुप्रिन्ट CC0 अन्तर्गत जारी गरिएको छ। तपाईं अनुमति नसोधी प्रतिलिपि, परिमार्जन, वितरण र प्रयोग गर्न सक्नुहुन्छ।
ब्लुप्रिन्ट मार्फत उत्पादनहरू किनेर सिर्जनाकर्तालाई सहयोग गर्नुहोस् सिर्जनाकर्ता कमिसन विक्रेताले तोकेको, वा यो ब्लुप्रिन्टको नयाँ संस्करण बनाउनुहोस् र आम्दानी बाँड्न आफ्नो ब्लुप्रिन्टमा जडानको रूपमा समावेश गर्नुहोस्।