Metal Oxide Varistor: Pure Zinc Oxide, Bismuth-Manganese Oxide Paste Fired On (Masuyama 1972, Ex. 7)
A varistor whose bismuth oxide and manganese dioxide are both fired on from a paste: pure zinc oxide, sintered at 1350 °C, coated with a 70 : 30 bismuth oxide and manganese dioxide paste and fired at 800 °C. The disc measured a C-value of 200 at 1 mA and a nonlinearity exponent n of 12.7.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 7. Unknown: how the aluminium is sprayed on, what the silver paint is, and how strong the epoxy solution of the paste is. The 10 g batch is our arithmetic. Picture: the patent's drawing.
उन्नत
2 days
निर्देशनहरू
1
1
Weigh zinc oxide and wet-mill 5 hours
Weigh zinc oxide and wet-mill 5 hours
Take pure zinc oxide (Table 9: 100 mole %). Mill wet for 5 hours, then dry, as in Example 1. Unknown: the milling liquid.
यस चरणका सामग्री:
जिंक अक्साइड धुलो10 ग्रामचाहिने औजार:
समभुज तराजु
फलामे बल मिल
सुकाउने भट्टी2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press discs 13 mm across and 2.5 mm thick at 340 kg/cm², as in Example 1.
चाहिने औजार:
हाइड्रोलिक प्रेस
डिस्क थिच्ने डाइ
भर्नियर क्यालिपर3
3
Sinter 1 hour at 1350 °C and furnace-cool
Sinter 1 hour at 1350 °C and furnace-cool
Sinter in air at 1350 °C for 1 hour and let the discs cool in the furnace.
चाहिने औजार:
मफल भट्टी4
4
Lap both faces
Lap both faces
Lap both faces with silicon carbide abrasive. Example 7 gives no thickness.
चाहिने औजार:
सिलिकन कार्बाइडका दानाभर्नियर क्यालिपर5
5
Coat with bismuth and manganese oxide paste, fire at 800 °C
Coat with bismuth and manganese oxide paste, fire at 800 °C
Coat both lapped faces with a paste whose solids are 70 % bismuth oxide and 30 % manganese dioxide by weight, and fire it in air at 800 °C for 30 minutes. Example 7 does not name the paste's liquid; ours: the epoxy-resin butyl-alcohol solution of Example 4. Not given: how much paste.
यस चरणका सामग्री:
बिस्मथ अक्साइड1 as required
म्याङ्गनिज डाइअक्साइड (पाइरोलुसाइट)1 as requiredचाहिने औजार:
इपोक्सी राल
n-ब्युटानोलमफल भट्टी6
6
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint, as in Example 1. Unknown: the spraying method and the paint.
यस चरणका सामग्री:
एल्युमिनियमको ढिक्का1 as required
चाँदीको सुचालक रङ1 as required
तामाको तार2 टुक्राचाहिने औजार:
धातु छर्कने अज्ञात विधिभर्नियर क्यालिपरसामग्री
6- 10 ग्रामप्लेसहोल्डर
- 1 as requiredप्लेसहोल्डर
- 1 as requiredप्लेसहोल्डर
- 1 as requiredप्लेसहोल्डर
- 1 as requiredप्लेसहोल्डर
- 2 टुक्राप्लेसहोल्डर
आवश्यक उपकरणहरू
11- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
यो खाकाले बनाउँछ
सम्बन्धित ब्लुप्रिन्ट
यी ब्लुप्रिन्टहरूले ज्ञान साझा गर्छन् — प्रविधि, सामग्री वा सिद्धान्त
CC0 सार्वजनिक डोमेन
यो ब्लुप्रिन्ट CC0 अन्तर्गत जारी गरिएको छ। तपाईं अनुमति नसोधी प्रतिलिपि, परिमार्जन, वितरण र प्रयोग गर्न सक्नुहुन्छ।
ब्लुप्रिन्ट मार्फत उत्पादनहरू किनेर सिर्जनाकर्तालाई सहयोग गर्नुहोस् सिर्जनाकर्ता कमिसन विक्रेताले तोकेको, वा यो ब्लुप्रिन्टको नयाँ संस्करण बनाउनुहोस् र आम्दानी बाँड्न आफ्नो ब्लुप्रिन्टमा जडानको रूपमा समावेश गर्नुहोस्।