Ferrite Toroid Core: Wet-Process Copper-Zinc Ferrite with a Stepped Anneal Down to 310 °C (Snoek 1948)
The wet-process copper-zinc ferrite ring of Snoek's Example II, given a long stepped anneal in oxygen after its 600 °C hold: 19 hours at 510 °C, 34 hours at 410 °C and 12 hours at 310 °C. The initial permeability fell from 500 to 410.
Source: J. L. Snoek, US 2,452,529 (Philips, 1948), Example II, wet process. Picture: our diagram.
Abantado
3 days
Mga Tagubilin
1
1
Dissolve the copper, zinc and iron salts
Dissolve the copper, zinc and iron salts
Make 1 litre of a purified solution of 0.2 mol copper sulphate, 0.3 mol zinc sulphate and 1 mol iron nitrate. Ours: 49.94 g copper sulphate pentahydrate; weigh the zinc sulphate and ferric nitrate for the hydrate you have.
Mga materyales para sa hakbang na ito:
Copper sulfate pentahydrate (CuSO4·5H2O)49.94 g
Zinc sulfate0.3 mol
Ferric nitrate1 mol
Distiladong Tubig1 lMga kailangang kasangkapan:
Timbangang panimbang
Basong Borosilikato
Gwantes na goma2
2
Precipitate hot with 9 M caustic soda
Precipitate hot with 9 M caustic soda
Heat the solution and precipitate it with 0.5 litre of 9 molar caustic soda. Ours: 180 g sodium hydroxide in water to 0.5 litre. Strong alkali: goggles and gloves.
Mga materyales para sa hakbang na ito:
Sodium Hydroxide — Uring Panlaboratoryo180 gMga kailangang kasangkapan:
Basong Borosilikato
Pang-init na Plato
Salamin Laban sa Tilamsik ng KemikalGwantes na goma3
3
Wash, dry and pre-heat at 700 °C
Wash, dry and pre-heat at 700 °C
Wash out the deposit, dry it, and pre-heat it at 700 °C so it moulds better.
Mga kailangang kasangkapan:
Papel na PansalaDistiladong Tubig
Hurnong pantuyo
Hurnong Tubo
Krisol na may takip (porselana)
Guwantes na Matibay sa Init4
4
Mould a ring at 4 tons per cm²
Mould a ring at 4 tons per cm²
Mould the powder at 4 tons per square centimetre into a ring 3 cm across with a 4 × 4 mm section.
Mga kailangang kasangkapan:
Haydroliko na pandiin
Dais na Pang-Press ng Singsing
Maskara Laban sa Alikabok5
5
Heat 3 hours at 900 °C, cool to 600 °C, hold 30 hours
Heat 3 hours at 900 °C, cool to 600 °C, hold 30 hours
Heat the ring for about 3 hours at 900 °C, cool it to 600 °C at 5 °C per minute, hold it there for 30 hours and let it cool to room temperature, all in a current of oxygen. Snoek's core: initial permeability 500.
Mga kailangang kasangkapan:
Hurnong Tubo
Oksiheno
Tangke ng gas na may presyon
Pirometro
Sipit ng KrisolGuwantes na Matibay sa Init6
6
Anneal 19 h at 510 °C, 34 h at 410 °C, 12 h at 310 °C
Anneal 19 h at 510 °C, 34 h at 410 °C, 12 h at 310 °C
After the 600 °C hold, keep the core for another 19 hours at 510 °C, 34 hours at 410 °C and 12 hours at 310 °C, all in oxygen. Snoek's core: initial permeability 410.
Mga kailangang kasangkapan:
Hurnong TuboOksihenoTangke ng gas na may presyonPirometroSipit ng KrisolGuwantes na Matibay sa InitMga Materyales
5- Placeholder
- 0.3 molPlaceholder
- 1 molPlaceholder
- Placeholder
- Placeholder
Mga Kinakailangang Kasangkapan
18- Placeholder
- Placeholder
- Placeholder
- Placeholder
- Placeholder
- Placeholder
- Placeholder
- Placeholder
- Placeholder
- Placeholder
- Placeholder
- Placeholder
- Placeholder
- Placeholder
- Placeholder
- Placeholder
- Placeholder
- Placeholder
Ang blueprint na ito ay gumagawa ng
Kaugnay na Blueprint
Ang mga blueprint na ito ay nagbabahagi ng kaalaman — mga teknik, materyales, o prinsipyo
CC0 Pampublikong Domain
Ang blueprint na ito ay inilabas sa ilalim ng CC0. Malaya kang kumopya, magbago, mamahagi, at gumamit nang walang pahintulot.
Suportahan ang Maker sa pamamagitan ng pagbili ng mga produkto sa kanilang Blueprint Komisyon ng Maker itinakda ng mga Vendor, o lumikha ng bagong bersyon ng Blueprint na ito at isama bilang koneksyon sa iyong Blueprint upang ibahagi ang kita.