PTFE Fine Powder: a Dispersion Stirred Until It Curdles (Lontz 1952)
A PTFE dispersion is stable on the shelf, but stirred hard enough it curdles. Fifty seconds at 1000 rpm in a baffled beaker and the polymer floats up as a dry-looking, unwettable crumb. Washed and dried, it is a free-flowing powder for rolling into tape, or for cold lubricated extrusion.
Source: J. F. Lontz (du Pont), US 2,593,583 (1952), Example 1. Lontz started from a dispersion made with disuccinic acid peroxide; ours is Berry's persulfate dispersion, diluted to his 17 %. Picture drawn by Youblob.
Hagati
1 day
Amabwiriza
1
1
Dilute the dispersion to 17 %
Dilute the dispersion to 17 %
Ours: stir the 34 % dispersion with an equal weight of distilled water to get 17 % solids, the strength Lontz used.
Ibikoresho by'iyi ntambwe:
Ikwirakwizwa rya PTFE mu mazi1 part
Amazi Yatunganyijwe1 partIbikoresho bikenewe:
Umunzani w'ibiro
Icupa ry'Ikirahure Rifite Umufuniko2
2
Set up the baffled beaker
Set up the baffled beaker
A 1-gallon stainless beaker, 6.5 in across and 7.5 in deep, with four baffles about ⅜ × 1 in hanging from the cover to within 3 in of the bottom. Stirrer: open turbine, 4 blades 1½ in high, 5 in across, reaching to within 1 in of the bottom.
Ibikoresho bikenewe:
Ikigega cyo kuvanga gifite inzitizi
Igikoresho cyo kuvanga3
3
Stir hard at 176 °F for 50 seconds
Stir hard at 176 °F for 50 seconds
Put in half a gallon of the 17 % dispersion and heat it to 176 °F (80 °C). Run the stirrer at 1000 rpm for 50 seconds (Lontz measured 0.72 hp per gallon). The polymer coagulates and floats, unwetted, on top.
Ibikoresho bikenewe:
Ikigega cyo kuvanga gifite inzitiziIgikoresho cyo kuvanga
Urubaho rushyushya
Igipima Ubushyuhe4
4
Wash hot, then cold
Wash hot, then cold
Pour off the water. Wash the polymer with hot water at 176 °F, then with cold water at 60 °F (16 °C), and drain.
Ibikoresho bikenewe:
Ikigega cyo kuvanga gifite inzitiziIgipima Ubushyuhe5
5
Dry at 230 °F for 16 hours
Dry at 230 °F for 16 hours
Spread the wet polymer on a 100-mesh screen and dry it in an oven at 230 °F (110 °C) for 16 hours. It comes out a free-flowing granular powder that passes 6–8 mesh.
Ibikoresho bikenewe:
Akayunguruzo k'insinga nziza
Ifuru yo kumishahoIcupa ry'Ikirahure Rifite UmufunikoIbikoresho
2- Umwanya
- 1 partUmwanya
Ibikoresho bikenewe
8- Umwanya
- Umwanya
- Umwanya
- Umwanya
- Umwanya
- Umwanya
Iki gishushanyo gikora
Blueprint zijyanye
Izi blueprint zisangira ubumenyi — uburyo, ibikoresho cyangwa amahame
CC0 Umurenge rusange
Iyi blueprint yasohowe munsi ya CC0. Ushobora gukoporora, guhindura, gukwirakwiza no gukoresha nta kwemererwa.
Shyigikira Umuremyi ugura ibicuruzwa binyuze muri Blueprint ye Komisiyo y'Umuremyi byashyizweho n'Abacuruzi, cyangwa kora verisiyo nshya y'iyi Blueprint ukayinjiza nk'isano muri Blueprint yawe kugira ngo musangire inyungu.