Barium-Calcium Ferrite Disc Magnet: 0.09 mol BaCO3 and 0.01 mol CaCO3 (Went, Philips 1956, Ex. 19)
A ceramic magnet with a tenth of the barium replaced by calcium: 0.09 mol barium carbonate and 0.01 mol calcium carbonate to 0.6 mol iron oxide, made as in Example 18: milled, presintered at 1000 °C, milled again, formed and passed through a 1330 °C furnace in 10 minutes. Went's rod held 1,705 gauss with a coercive force of 1,110 oersted.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 19. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
İleri
2 days
Talimatlar
1
1
Weigh barium carbonate, chalk and iron oxide
Weigh barium carbonate, chalk and iron oxide
Weigh 17.76 g barium carbonate (0.09 mol), 1.001 g calcium carbonate (0.01 mol) and 95.55 g ferric oxide (0.6 mol). Barium carbonate is poisonous if swallowed: gloves and a dust respirator.
Bu adım için malzemeler:
Baryum karbonat (viterit)17.76 g
Kalsiyum karbonat (tebeşir tozu)1.001 g
Ferrik oksit95.55 gGerekli aletler:
Eşit kollu terazi
Lastik eldiven
P100 Solunum Maskesi2
2
Mill with alcohol 4 hours, dry at 150 °C
Mill with alcohol 4 hours, dry at 150 °C
Grind with alcohol in a ball mill for 4 hours and dry in air at 150 °C.
Gerekli aletler:
Demir Bilyalı Değirmen
Etanol - laboratuvar kalitesi, %95
Kurutma fırını3
3
Presinter in air at 1000 °C for 2 hours
Presinter in air at 1000 °C for 2 hours
Fire in air at 1000 °C for 2 hours.
Gerekli aletler:
Mufla fırın
Kapaklı kroze (porselen)
Pota Maşası
Isıya Dayanıklı Eldiven4
4
Mill again 4 hours, dry, form
Mill again 4 hours, dry, form
Grind again with alcohol for 4 hours and dry. Example 19 extrudes a rod; ours: press discs at 1.5 tonnes per cm², as Example 18 moulds its rod.
Gerekli aletler:
Demir Bilyalı DeğirmenEtanol - laboratuvar kalitesi, %95Kurutma fırını
Hidrolik pres
Disk presleme kalıbı5
5
Pass through a 1330 °C zone in 10 minutes
Pass through a 1330 °C zone in 10 minutes
Sinter at 1330 °C by passing the pieces through a 10 cm hot zone at 10 mm per minute: 10 minutes in the heat.
Gerekli aletler:
Tüp FırınIsıya Dayanıklı Eldiven6
6
Magnetise the discs
Magnetise the discs
The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.
Gerekli aletler:
Elektromıknatıs
PusulaMalzemeler
3- 17.76 gYer Tutucu
- Yer Tutucu
- 95.55 gYer Tutucu
Gerekli Aletler
15- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
Bu planla yapılan
İlgili Blueprint'ler
Bu blueprint'ler bilgi paylaşır — teknikler, malzemeler veya ilkeler
CC0 Kamu Malı
Bu plan CC0 lisansıyla yayınlanmıştır. İzin almadan kopyalayabilir, değiştirebilir, dağıtabilir ve herhangi bir amaçla kullanabilirsiniz.
Planı üzerinden ürün satın alarak Maker'ı destekleyin, böylece Maker Komisyonu Satıcılar tarafından belirlenen komisyonu kazanırlar veya bu Planın yeni bir versiyonunu oluşturun ve gelir paylaşımı için kendi Planınıza bağlantı olarak ekleyin.