Barium Ferrite Disc Magnet from Natural Magnetite, Presintered at 900 °C (Went, Philips 1956, Ex. 36, Procedure 1)
A barium ferrite magnet made from natural magnetite instead of ferric oxide: barium carbonate and magnetite ground 18 hours, presintered 3 hours at 900 °C, ground again 18 hours, pressed and sintered 2 hours at 1200 °C. Went's rod held 1,450 gauss with a coercive force of 2,425 oersted.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 36. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
İleri
2 days
Talimatlar
1
1
Weigh barium carbonate and magnetite
Weigh barium carbonate and magnetite
Weigh 9.9 g barium carbonate (0.05 mol) and 46.9 g natural magnetite, Fe3O4 (0.20 mol). Barium carbonate is poisonous if swallowed: gloves and a dust respirator.
Bu adım için malzemeler:
Baryum karbonat (viterit)9.9 g
Manyetit46.9 gGerekli aletler:
Eşit kollu terazi
Lastik eldiven
P100 Solunum Maskesi2
2
Grind 18 hours in a ball mill
Grind 18 hours in a ball mill
Grind the mixture in a ball mill for 18 hours. The patent does not say whether wet or dry.
Gerekli aletler:
Demir Bilyalı DeğirmenP100 Solunum Maskesi3
3
Presinter at 900 °C for 3 hours
Presinter at 900 °C for 3 hours
Fire the ground mixture at 900 °C for three hours and let it cool.
Gerekli aletler:
Mufla fırın
Kapaklı kroze (porselen)
Pota Maşası
Isıya Dayanıklı Eldiven4
4
Grind 18 hours in a ball mill
Grind 18 hours in a ball mill
Grind it again in a ball mill for 18 hours. The patent does not say whether wet or dry.
Gerekli aletler:
Demir Bilyalı DeğirmenP100 Solunum Maskesi5
5
Press at 1.5 t/cm²
Press at 1.5 t/cm²
Press at 1.5 tonnes per cm² (ours: discs instead of a rod).
Gerekli aletler:
Hidrolik pres
Disk presleme kalıbı6
6
Sinter at 1200 °C for 2 hours
Sinter at 1200 °C for 2 hours
Sinter at 1200 °C for 2 hours. The patent gives no atmosphere for this example. Went's rod: 1,450 gauss, 2,425 oersted.
Gerekli aletler:
Mufla fırınPota MaşasıIsıya Dayanıklı Eldiven7
7
Magnetise the discs
Magnetise the discs
The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.
Gerekli aletler:
Elektromıknatıs
PusulaGerekli Aletler
12- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
Bu planla yapılan
İlgili Blueprint'ler
Bu blueprint'ler bilgi paylaşır — teknikler, malzemeler veya ilkeler
CC0 Kamu Malı
Bu plan CC0 lisansıyla yayınlanmıştır. İzin almadan kopyalayabilir, değiştirebilir, dağıtabilir ve herhangi bir amaçla kullanabilirsiniz.
Planı üzerinden ürün satın alarak Maker'ı destekleyin, böylece Maker Komisyonu Satıcılar tarafından belirlenen komisyonu kazanırlar veya bu Planın yeni bir versiyonunu oluşturun ve gelir paylaşımı için kendi Planınıza bağlantı olarak ekleyin.