Barium Ferrite Disc Magnet: Example 7 Without the Orienting Field (Gorter, Philips 1956, Ex. 7 Comparison)
Made as in Example 7 but without the first, orienting field. Gorter's comparison blocks held 2,250 gauss with a coercive force of 1,850 oersted and a (BH)max of 0.95 × 10⁶.
Source: E. W. Gorter, G. W. Rathenau and A. L. Stuyts (Philips), US 2,762,778 (1956), Example 7. They made blocks; disc size is ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
İleri
3 days
Talimatlar
1
1
Weigh barium carbonate and iron oxide
Weigh barium carbonate and iron oxide
Weigh 450 g barium carbonate and 2000 g ferric oxide. Barium carbonate is poisonous if swallowed: gloves and a dust respirator.
Bu adım için malzemeler:
Baryum karbonat (viterit)450 g
Ferrik oksit2000 gGerekli aletler:
Eşit kollu terazi
Lastik eldiven
P100 Solunum Maskesi2
2
Mill 20 hours under alcohol, dry
Mill 20 hours under alcohol, dry
Grind the mixture in a ball mill under alcohol for 20 hours, then dry it.
Gerekli aletler:
Demir Bilyalı Değirmen
Etanol - laboratuvar kalitesi, %95
Kurutma fırını3
3
Pre-fire: through a 1100 °C zone in 10 minutes
Pre-fire: through a 1100 °C zone in 10 minutes
Pass the dry powder at 20 mm per minute through an electric furnace with a 20 cm hot zone at 1100 °C, in air: 10 minutes in the heat. Let it cool.
Gerekli aletler:
Tüp Fırın
Kapaklı kroze (porselen)
Isıya Dayanıklı Eldiven4
4
Grind 48 hours with alcohol, dry
Grind 48 hours with alcohol, dry
Pulverise the pre-fired material in a ball mill with alcohol for 48 hours, then dry it. This is the pre-fired powder.
Gerekli aletler:
Demir Bilyalı DeğirmenEtanol - laboratuvar kalitesi, %95Kurutma fırını5
5
Stir into 8 % polyvinyl acetate in acetone
Stir into 8 % polyvinyl acetate in acetone
Dissolve polyvinyl acetate in acetone to a 8 % solution and stir the pre-fired powder into it, 1 cc of solution per gram of powder. The binder burns off later.
Gerekli aletler:
Polivinil Asetat
AsetonEşit kollu terazi6
6
Mould without a first field
Mould without a first field
Put the suspension in a moulding die and remove the binder solution without any magnetic field. This is the patent's comparison block.
Gerekli aletler:
Disk presleme kalıbı
Hidrolik pres7
7
Heat to 500 °C in a 2000 oersted field
Heat to 500 °C in a 2000 oersted field
Put the block in an electric furnace between the magnet's poles. With a second field of 2000 oersted along the first field's direction, heat to 500 °C, which burns off the rest of the binder. Then switch the field off.
Gerekli aletler:
Tüp Fırın
ElektromıknatısIsıya Dayanıklı Eldiven8
8
Sinter: through a 1280 °C zone in 5 minutes
Sinter: through a 1280 °C zone in 5 minutes
Pass the block at 20 mm per minute through an electric furnace in air at 1280 °C with a 10 cm hot zone: about 5 minutes in the heat.
Gerekli aletler:
Tüp FırınIsıya Dayanıklı Eldiven9
9
Magnetise the block
Magnetise the block
Magnetise the block in a field. Without the orienting field it has no preferred direction. Ours: an electromagnet. Find the north face with a compass.
Gerekli aletler:
Elektromıknatıs
PusulaMalzemeler
2- Yer Tutucu
- 2000 gYer Tutucu
Gerekli Aletler
15- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
Bu planla yapılan
İlgili Blueprint'ler
Bu blueprint'ler bilgi paylaşır — teknikler, malzemeler veya ilkeler
CC0 Kamu Malı
Bu plan CC0 lisansıyla yayınlanmıştır. İzin almadan kopyalayabilir, değiştirebilir, dağıtabilir ve herhangi bir amaçla kullanabilirsiniz.
Planı üzerinden ürün satın alarak Maker'ı destekleyin, böylece Maker Komisyonu Satıcılar tarafından belirlenen komisyonu kazanırlar veya bu Planın yeni bir versiyonunu oluşturun ve gelir paylaşımı için kendi Planınıza bağlantı olarak ekleyin.