Oriented Strontium Ferrite Disc Magnet: Agate-Milled, 10,000 Oersted Field (Gorter, Philips 1956, Ex. 8)
Omegatron (Wikimedia Commons) · CC BY-SA 3.0
Charlie

Oluşturan

Charlie

28. Ekim 2026DE
2
0
0
0
0

Oriented Strontium Ferrite Disc Magnet: Agate-Milled, 10,000 Oersted Field (Gorter, Philips 1956, Ex. 8)

A strontium ferrite magnet oriented in a magnetic field: strontium carbonate and iron oxide milled, pre-fired 2 hours at 1000 °C, ground fine in an agate mill, then oriented, heated and sintered as in Example 4. In the principal direction it held 2,640 gauss with a coercive force of 2,825 oersted and a (BH)max of 1.63 × 10⁶. Source: E. W. Gorter, G. W. Rathenau and A. L. Stuyts (Philips), US 2,762,778 (1956), Example 8. They made blocks; disc size is ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
İleri
3 days

Talimatlar

1

Weigh strontium carbonate and iron oxide

Weigh 29.5 g strontium carbonate and 179 g ferric oxide.

Bu adım için malzemeler:

Stronsiyum karbonatStronsiyum karbonat29.5 g
Ferrik oksitFerrik oksit179 g

Gerekli aletler:

Eşit kollu teraziEşit kollu terazi
P100 Solunum MaskesiP100 Solunum Maskesi
2

Mill 15 hours with alcohol, dry

Grind in a ball mill with alcohol for 15 hours. Remove the alcohol and dry the powder.

Gerekli aletler:

Demir Bilyalı DeğirmenDemir Bilyalı Değirmen
Etanol - laboratuvar kalitesi, %95Etanol - laboratuvar kalitesi, %95
Kurutma fırınıKurutma fırını
3

Pre-fire 2 hours at 1000 °C in air

Heat the powder for 2 hours at 1000 °C in an electric furnace in air. Let it cool.

Gerekli aletler:

Mufla fırınMufla fırın
Kapaklı kroze (porselen)Kapaklı kroze (porselen)
Pota MaşasıPota Maşası
Isıya Dayanıklı EldivenIsıya Dayanıklı Eldiven
4

Grind 4 hours in an agate centrifugal mill

Grind the cooled material for 4 hours with alcohol in an agate centrifugal mill, then dry it. This is the pre-fired powder.

Gerekli aletler:

Akik santrifüj değirmeniAkik santrifüj değirmeni
Etanol - laboratuvar kalitesi, %95Etanol - laboratuvar kalitesi, %95
Kurutma fırınıKurutma fırını
5

Stir into 8 % polyvinyl acetate in acetone

Dissolve polyvinyl acetate in acetone to a 8 % solution and stir the pre-fired powder into it, 1 cc of solution per gram of powder. The binder burns off later.

Gerekli aletler:

Polivinil AsetatPolivinil Asetat
AsetonAseton
Eşit kollu teraziEşit kollu terazi
6

Orient in a 10000 oersted field

Put the suspension in a moulding die between the poles of a magnet and apply a first field of 10000 oersted. Remove the binder solution while the field is on.

Gerekli aletler:

Disk presleme kalıbıDisk presleme kalıbı
ElektromıknatısElektromıknatıs
Hidrolik presHidrolik pres
7

Heat to 500 °C in a 2000 oersted field

Put the block in an electric furnace between the magnet's poles. With a second field of 2000 oersted along the first field's direction, heat to 500 °C, which burns off the rest of the binder. Then switch the field off.

Gerekli aletler:

Tüp FırınTüp Fırın
ElektromıknatısElektromıknatıs
Isıya Dayanıklı EldivenIsıya Dayanıklı Eldiven
8

Sinter: through a 1280 °C zone in 5 minutes

Pass the block at 20 mm per minute through an electric furnace in air at 1280 °C with a 10 cm hot zone: about 5 minutes in the heat.

Gerekli aletler:

Tüp FırınTüp Fırın
Isıya Dayanıklı EldivenIsıya Dayanıklı Eldiven
9

Magnetise in the principal direction

Magnetise the block along the direction of the first field, the principal direction. The patent magnetises it in a field in that direction; ours: an electromagnet. Find the north face with a compass.

Gerekli aletler:

ElektromıknatısElektromıknatıs
PusulaPusula

Malzemeler

2

Gerekli Aletler

17

Bu planla yapılan

Thumbnail
Yer tutucu

Disk Mıknatıs

Free

2
0
1

İlgili Blueprint'ler

Bu blueprint'ler bilgi paylaşır — teknikler, malzemeler veya ilkeler

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

Charlie tarafındanDE

Endüstriyel

1
0
0
0
0
0
Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

Charlie tarafındanDE

Endüstriyel

4
0
0
0
0
0

CC0 Kamu Malı

Bu plan CC0 lisansıyla yayınlanmıştır. İzin almadan kopyalayabilir, değiştirebilir, dağıtabilir ve herhangi bir amaçla kullanabilirsiniz.

Planı üzerinden ürün satın alarak Maker'ı destekleyin, böylece Maker Komisyonu Satıcılar tarafından belirlenen komisyonu kazanırlar veya bu Planın yeni bir versiyonunu oluşturun ve gelir paylaşımı için kendi Planınıza bağlantı olarak ekleyin.

Tartışma

(0)

Giriş yapın tartışmaya katılmak için

Yorumlar yükleniyor...