Strontium Ferrite Disc Magnet: 0.7 mol SrCO3 to 3.2 mol Iron Oxide, 1280 °C (Went, Philips 1956, Ex. 12)
Omegatron (Wikimedia Commons) · CC BY-SA 3.0
Charlie

Oluşturan

Charlie

28. Ekim 2026DE
1
0
0
0
0

Strontium Ferrite Disc Magnet: 0.7 mol SrCO3 to 3.2 mol Iron Oxide, 1280 °C (Went, Philips 1956, Ex. 12)

A strontium ferrite: 0.7 mol strontium carbonate to 3.2 mol iron oxide, milled, bound and formed as in Example 4, and passed through a 1280 °C furnace in 10 minutes. Went's rod held 1,955 gauss with a coercive force of 2,900 oersted. Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 12. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
İleri
2 days

Talimatlar

1

Weigh strontium carbonate and iron oxide

Weigh 103.3 g strontium carbonate (0.7 mol) and 503.0 g ferric oxide (3.2 mol).

Bu adım için malzemeler:

Stronsiyum karbonatStronsiyum karbonat103.3 g
Ferrik oksitFerrik oksit503 g

Gerekli aletler:

Eşit kollu teraziEşit kollu terazi
P100 Solunum MaskesiP100 Solunum Maskesi
2

Mill with alcohol 15.5 hours, dry and sieve

As in Example 4: grind the mixture with alcohol in a ball mill for 15.5 hours, then dry it and sieve it.

Gerekli aletler:

Demir Bilyalı DeğirmenDemir Bilyalı Değirmen
Etanol - laboratuvar kalitesi, %95Etanol - laboratuvar kalitesi, %95
Kurutma fırınıKurutma fırını
KalburKalbur
3

Knead with a binder and form

Mix 300 g of the powder with a binder such as polyvinyl alcohol (Went names it or nitrocellulose) into a kneadable mass. The patent extrudes rods about 3 mm across; ours: press discs at 1.5 tonnes per cm², as in its other examples. Dry them in air for about 24 hours.

Gerekli aletler:

Polivinil alkol tozuPolivinil alkol tozu
Hidrolik presHidrolik pres
Disk presleme kalıbıDisk presleme kalıbı
Kurutma fırınıKurutma fırını
4

Pass through a 1280 °C zone in 10 minutes

Sinter in air at 1280 °C by passing the pieces through a 10 cm hot zone at 10 mm per minute: 10 minutes in the heat.

Gerekli aletler:

Tüp FırınTüp Fırın
Isıya Dayanıklı EldivenIsıya Dayanıklı Eldiven
5

Magnetise the discs

The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.

Gerekli aletler:

ElektromıknatısElektromıknatıs
PusulaPusula

Malzemeler

2

Gerekli Aletler

13

Bu planla yapılan

Thumbnail
Yer tutucu

Disk Mıknatıs

Free

2
0
1

İlgili Blueprint'ler

Bu blueprint'ler bilgi paylaşır — teknikler, malzemeler veya ilkeler

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

Charlie tarafındanDE

Endüstriyel

1
0
0
0
0
0
Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

Charlie tarafındanDE

Endüstriyel

4
0
0
0
0
0

CC0 Kamu Malı

Bu plan CC0 lisansıyla yayınlanmıştır. İzin almadan kopyalayabilir, değiştirebilir, dağıtabilir ve herhangi bir amaçla kullanabilirsiniz.

Planı üzerinden ürün satın alarak Maker'ı destekleyin, böylece Maker Komisyonu Satıcılar tarafından belirlenen komisyonu kazanırlar veya bu Planın yeni bir versiyonunu oluşturun ve gelir paylaşımı için kendi Planınıza bağlantı olarak ekleyin.

Tartışma

(0)

Giriş yapın tartışmaya katılmak için

Yorumlar yükleniyor...