Strontium Ferrite Disc Magnet: 0.6 mol SrCO3 to 3 mol Iron Oxide, 1280 °C (Went, Philips 1956, Ex. 13)
A strontium ferrite: 0.6 mol strontium carbonate to 3 mol iron oxide, milled, bound and formed as in Example 4, and passed through a 1280 °C furnace in 10 minutes. Went's rod held 2,100 gauss with a coercive force of 2,800 oersted.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 13. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
İleri
2 days
Talimatlar
1
1
Weigh strontium carbonate and iron oxide
Weigh strontium carbonate and iron oxide
Weigh 88.6 g strontium carbonate (0.6 mol) and 479.0 g ferric oxide (3 mol).
Bu adım için malzemeler:
Stronsiyum karbonat88.6 g
Ferrik oksit479 gGerekli aletler:
Eşit kollu terazi
P100 Solunum Maskesi2
2
Mill with alcohol 15.5 hours, dry and sieve
Mill with alcohol 15.5 hours, dry and sieve
As in Example 4: grind the mixture with alcohol in a ball mill for 15.5 hours, then dry it and sieve it.
Gerekli aletler:
Demir Bilyalı Değirmen
Etanol - laboratuvar kalitesi, %95
Kurutma fırını
Kalbur3
3
Knead with a binder and form
Knead with a binder and form
Mix 300 g of the powder with a binder such as polyvinyl alcohol (Went names it or nitrocellulose) into a kneadable mass. The patent extrudes rods about 3 mm across; ours: press discs at 1.5 tonnes per cm², as in its other examples. Dry them in air for about 24 hours.
Gerekli aletler:
Polivinil alkol tozu
Hidrolik pres
Disk presleme kalıbıKurutma fırını4
4
Pass through a 1280 °C zone in 10 minutes
Pass through a 1280 °C zone in 10 minutes
Sinter in air at 1280 °C by passing the pieces through a 10 cm hot zone at 10 mm per minute: 10 minutes in the heat.
Gerekli aletler:
Tüp Fırın
Isıya Dayanıklı Eldiven5
5
Magnetise the discs
Magnetise the discs
The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.
Gerekli aletler:
Elektromıknatıs
PusulaMalzemeler
2- 88.6 gYer Tutucu
- 479 gYer Tutucu
Gerekli Aletler
13- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
Bu planla yapılan
İlgili Blueprint'ler
Bu blueprint'ler bilgi paylaşır — teknikler, malzemeler veya ilkeler
CC0 Kamu Malı
Bu plan CC0 lisansıyla yayınlanmıştır. İzin almadan kopyalayabilir, değiştirebilir, dağıtabilir ve herhangi bir amaçla kullanabilirsiniz.
Planı üzerinden ürün satın alarak Maker'ı destekleyin, böylece Maker Komisyonu Satıcılar tarafından belirlenen komisyonu kazanırlar veya bu Planın yeni bir versiyonunu oluşturun ve gelir paylaşımı için kendi Planınıza bağlantı olarak ekleyin.