Strontium Ferrite Disc Magnet: Presintered at 1100 °C, 0.1 mol SrCO3 to 0.7 mol Iron Oxide (Went, Philips 1956, Ex. 8)
Omegatron (Wikimedia Commons) · CC BY-SA 3.0
Charlie

Oluşturan

Charlie

28. Ekim 2026DE
1
0
0
0
0

Strontium Ferrite Disc Magnet: Presintered at 1100 °C, 0.1 mol SrCO3 to 0.7 mol Iron Oxide (Went, Philips 1956, Ex. 8)

A strontium ferrite: 0.1 mol strontium carbonate to 0.7 mol iron oxide, dried, milled, presintered 3.5 hours at 1100 °C, bound, formed and passed through a 1280 °C furnace in 10 minutes. Went's rod held 1,535 gauss with a coercive force of 2,800 oersted. Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 8. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
İleri
2 days

Talimatlar

1

Weigh strontium carbonate and iron oxide

Weigh 14.8 g strontium carbonate (0.1 mol) and 112.1 g ferric oxide (0.7 mol).

Bu adım için malzemeler:

Stronsiyum karbonatStronsiyum karbonat14.8 g
Ferrik oksitFerrik oksit112.1 g

Gerekli aletler:

Eşit kollu teraziEşit kollu terazi
P100 Solunum MaskesiP100 Solunum Maskesi
2

Dry at 200 °C, mill with alcohol 4 hours

Dry the mixture at 200 °C, then grind it with alcohol in a ball mill for 4 hours and dry it.

Gerekli aletler:

Kurutma fırınıKurutma fırını
Demir Bilyalı DeğirmenDemir Bilyalı Değirmen
Etanol - laboratuvar kalitesi, %95Etanol - laboratuvar kalitesi, %95
3

Presinter in air at 1100 °C for 3.5 hours

Fire the powder in air at 1100 °C for about 3.5 hours.

Gerekli aletler:

Mufla fırınMufla fırın
Kapaklı kroze (porselen)Kapaklı kroze (porselen)
Pota MaşasıPota Maşası
Isıya Dayanıklı EldivenIsıya Dayanıklı Eldiven
4

Add a binder and form, dry overnight

Add a binder as in Example 1 (polyvinyl alcohol or nitrocellulose). The patent extrudes rods; ours: press discs at 1.5 tonnes per cm². Dry overnight.

Gerekli aletler:

Polivinil alkol tozuPolivinil alkol tozu
Hidrolik presHidrolik pres
Disk presleme kalıbıDisk presleme kalıbı
Kurutma fırınıKurutma fırını
5

Pass through a 1280 °C zone in 10 minutes

Sinter in air at 1280 °C by passing the pieces through a 10 cm hot zone at 10 mm per minute: 10 minutes in the heat.

Gerekli aletler:

Tüp FırınTüp Fırın
Isıya Dayanıklı EldivenIsıya Dayanıklı Eldiven
6

Magnetise the discs

The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.

Gerekli aletler:

ElektromıknatısElektromıknatıs
PusulaPusula

Malzemeler

2

Gerekli Aletler

15

Bu planla yapılan

Thumbnail
Yer tutucu

Disk Mıknatıs

Free

2
0
1

İlgili Blueprint'ler

Bu blueprint'ler bilgi paylaşır — teknikler, malzemeler veya ilkeler

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

Charlie tarafındanDE

Endüstriyel

1
0
0
0
0
0
Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

Charlie tarafındanDE

Endüstriyel

4
0
0
0
0
0

CC0 Kamu Malı

Bu plan CC0 lisansıyla yayınlanmıştır. İzin almadan kopyalayabilir, değiştirebilir, dağıtabilir ve herhangi bir amaçla kullanabilirsiniz.

Planı üzerinden ürün satın alarak Maker'ı destekleyin, böylece Maker Komisyonu Satıcılar tarafından belirlenen komisyonu kazanırlar veya bu Planın yeni bir versiyonunu oluşturun ve gelir paylaşımı için kendi Planınıza bağlantı olarak ekleyin.

Tartışma

(0)

Giriş yapın tartışmaya katılmak için

Yorumlar yükleniyor...