Metal Oxide Varistor: Zinc Oxide with 0.2 % Aluminium Oxide, Bismuth Oxide Paste Fired On (Masuyama 1972, Ex. 5)
A varistor with bismuth oxide fired on from a paste instead of mixed in: 99.8 % zinc oxide with 0.2 % aluminium oxide by moles, sintered at 1350 °C, coated with bismuth oxide paste and fired at 800 °C. The disc measured a C-value of 46 at 1 mA and a nonlinearity exponent n of 5.6.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 5. Unknown: how the aluminium is sprayed on, what the silver paint is, and how strong the epoxy solution of the paste is. The 10 g batch is our arithmetic. Picture: the patent's drawing.
İleri
2 days
Talimatlar
1
1
Weigh 99.8 : 0.2 and wet-mill 5 hours
Weigh 99.8 : 0.2 and wet-mill 5 hours
Mix zinc oxide and aluminium oxide 99.8 : 0.2 by moles. Ours, for 10 g: 9.975 g zinc oxide and 0.025 g aluminium oxide (our arithmetic). Mill wet for 5 hours, then dry, as in Example 1. Unknown: the milling liquid.
Bu adım için malzemeler:
Çinko Oksit Tozu9.975 g
Alümin tozu (alüminyum oksit)0.025 gGerekli aletler:
Eşit kollu terazi
Demir Bilyalı Değirmen
Kurutma fırını2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press discs 13 mm across and 2.5 mm thick at 340 kg/cm², as in Example 1.
Gerekli aletler:
Hidrolik pres
Disk presleme kalıbı
Kumpas3
3
Sinter 1 hour at 1350 °C and furnace-cool
Sinter 1 hour at 1350 °C and furnace-cool
As in Example 2: sinter in air at 1350 °C for 1 hour and let the discs cool in the furnace.
Gerekli aletler:
Mufla fırın4
4
Lap both faces
Lap both faces
Lap both faces with silicon carbide abrasive. Example 5 gives no thickness.
Gerekli aletler:
Silisyum karbür tanesiKumpas5
5
Coat with bismuth oxide paste and fire at 800 °C
Coat with bismuth oxide paste and fire at 800 °C
Coat both lapped faces with a paste of 50 % by weight bismuth oxide in a solution of epoxy resin in butyl alcohol, and fire it in air at 800 °C for 30 minutes. The bismuth oxide diffuses into the zinc oxide. Not given: how much paste, or the strength of the epoxy solution.
Bu adım için malzemeler:
Bizmut oksit1 as requiredGerekli aletler:
Epoksi reçine
n-ButanolMufla fırın6
6
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint, as in Example 1. Unknown: the spraying method and the paint.
Bu adım için malzemeler:
Alüminyum külçe1 as required
Gümüş iletken boya1 as required
Bakır Tel2 adetGerekli aletler:
Bilinmeyen metal püskürtme yöntemiKumpasMalzemeler
6- 9.975 gYer Tutucu
- Yer Tutucu
- 1 as requiredYer Tutucu
- 1 as requiredYer Tutucu
- 1 as requiredYer Tutucu
- 2 adetYer Tutucu
Gerekli Aletler
11- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
Bu planla yapılan
İlgili Blueprint'ler
Bu blueprint'ler bilgi paylaşır — teknikler, malzemeler veya ilkeler
CC0 Kamu Malı
Bu plan CC0 lisansıyla yayınlanmıştır. İzin almadan kopyalayabilir, değiştirebilir, dağıtabilir ve herhangi bir amaçla kullanabilirsiniz.
Planı üzerinden ürün satın alarak Maker'ı destekleyin, böylece Maker Komisyonu Satıcılar tarafından belirlenen komisyonu kazanırlar veya bu Planın yeni bir versiyonunu oluşturun ve gelir paylaşımı için kendi Planınıza bağlantı olarak ekleyin.