Metal Oxide Varistor: Zinc Oxide with 0.5 % Chromic Oxide, Bismuth Oxide Paste Fired On (Masuyama 1972, Ex. 5)
A varistor with bismuth oxide fired on from a paste instead of mixed in: 99.5 % zinc oxide with 0.5 % chromic oxide by moles, sintered at 1350 °C, coated with bismuth oxide paste and fired at 800 °C. The disc measured a C-value of 163 at 1 mA and a nonlinearity exponent n of 19.8.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 5. Unknown: how the aluminium is sprayed on, what the silver paint is, and how strong the epoxy solution of the paste is. The 10 g batch is our arithmetic. Picture: the patent's drawing.
Просунутий
2 days
Інструкції
1
1
Weigh 99.5 : 0.5 and wet-mill 5 hours
Weigh 99.5 : 0.5 and wet-mill 5 hours
Mix zinc oxide and chromic oxide 99.5 : 0.5 by moles. Ours, for 10 g: 9.907 g zinc oxide and 0.093 g chromic oxide (our arithmetic). Mill wet for 5 hours, then dry, as in Example 1. Unknown: the milling liquid.
Матеріали для цього кроку:
Порошок оксиду цинку9.907 г
Оксид хрому0.093 гНеобхідні інструменти ({count})
Важільні терези
Залізний кульовий млин
Сушильна піч2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press discs 13 mm across and 2.5 mm thick at 340 kg/cm², as in Example 1.
Необхідні інструменти ({count})
Гідравлічний прес
Прес-форма для дисків
Штангенциркуль3
3
Sinter 1 hour at 1350 °C and furnace-cool
Sinter 1 hour at 1350 °C and furnace-cool
As in Example 2: sinter in air at 1350 °C for 1 hour and let the discs cool in the furnace.
Необхідні інструменти ({count})
Муфельна піч4
4
Lap both faces
Lap both faces
Lap both faces with silicon carbide abrasive. Example 5 gives no thickness.
Необхідні інструменти ({count})
Порошок карбіду кремніюШтангенциркуль5
5
Coat with bismuth oxide paste and fire at 800 °C
Coat with bismuth oxide paste and fire at 800 °C
Coat both lapped faces with a paste of 50 % by weight bismuth oxide in a solution of epoxy resin in butyl alcohol, and fire it in air at 800 °C for 30 minutes. The bismuth oxide diffuses into the zinc oxide. Not given: how much paste, or the strength of the epoxy solution.
Матеріали для цього кроку:
Оксид бісмуту1 as requiredНеобхідні інструменти ({count})
Епоксидна смола
н-БутанолМуфельна піч6
6
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint, as in Example 1. Unknown: the spraying method and the paint.
Матеріали для цього кроку:
Алюмінієвий зливок1 as required
Срібна струмопровідна фарба1 as required
Мідний дріт2 штукНеобхідні інструменти ({count})
Невідомий спосіб металізації напиленнямШтангенциркульМатеріали
6- 9.907 гЗаповнювач
- 0.093 гЗаповнювач
- 1 as requiredЗаповнювач
- 1 as requiredЗаповнювач
- 1 as requiredЗаповнювач
- 2 штукЗаповнювач
Необхідні інструменти
11- Заповнювач
- Заповнювач
- Заповнювач
- Заповнювач
- Заповнювач
- Заповнювач
- Заповнювач
- Заповнювач
- Заповнювач
- Заповнювач
- Заповнювач
За цим кресленням виготовляють
Пов'язані креслення
Ці креслення діляться знаннями — техніки, матеріали або принципи
CC0 Суспільне надбання
Це креслення випущено під ліцензією CC0. Ви можете вільно копіювати, змінювати, поширювати та використовувати цю роботу для будь-яких цілей без запиту дозволу.
Підтримайте мейкера, купуючи продукти через його креслення, де він отримує Комісію мейкера встановлену вендорами, або створіть нову ітерацію цього креслення та включіть його як зв'язок у власне креслення для розподілу доходу.