Barium-Calcium Ferrite Disc Magnet: 0.09 mol BaCO3 and 0.01 mol CaCO3 (Went, Philips 1956, Ex. 19)
A ceramic magnet with a tenth of the barium replaced by calcium: 0.09 mol barium carbonate and 0.01 mol calcium carbonate to 0.6 mol iron oxide, made as in Example 18: milled, presintered at 1000 °C, milled again, formed and passed through a 1330 °C furnace in 10 minutes. Went's rod held 1,705 gauss with a coercive force of 1,110 oersted.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 19. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Nâng cao
2 days
Hướng dẫn
1
1
Weigh barium carbonate, chalk and iron oxide
Weigh barium carbonate, chalk and iron oxide
Weigh 17.76 g barium carbonate (0.09 mol), 1.001 g calcium carbonate (0.01 mol) and 95.55 g ferric oxide (0.6 mol). Barium carbonate is poisonous if swallowed: gloves and a dust respirator.
Vật liệu cho bước này:
Bari cacbonat (witherit)17.76 g
Canxi cacbonat (bột đá trắng)1.001 g
Oxit sắt(III)95.55 gCông cụ cần thiết:
Cân hai đĩa
Găng tay cao su
Mặt nạ phòng độc P1002
2
Mill with alcohol 4 hours, dry at 150 °C
Mill with alcohol 4 hours, dry at 150 °C
Grind with alcohol in a ball mill for 4 hours and dry in air at 150 °C.
Công cụ cần thiết:
Máy nghiền bi sắt
Etanol phẩm cấp thí nghiệm, 95 %
Lò sấy3
3
Presinter in air at 1000 °C for 2 hours
Presinter in air at 1000 °C for 2 hours
Fire in air at 1000 °C for 2 hours.
Công cụ cần thiết:
Lò muffle
Chén nung có nắp (sứ)
Kìm gắp nồi nấu kim loại
Găng tay chịu nhiệt4
4
Mill again 4 hours, dry, form
Mill again 4 hours, dry, form
Grind again with alcohol for 4 hours and dry. Example 19 extrudes a rod; ours: press discs at 1.5 tonnes per cm², as Example 18 moulds its rod.
Công cụ cần thiết:
Máy nghiền bi sắtEtanol phẩm cấp thí nghiệm, 95 %Lò sấy
Máy ép thủy lực
Khuôn ép đĩa5
5
Pass through a 1330 °C zone in 10 minutes
Pass through a 1330 °C zone in 10 minutes
Sinter at 1330 °C by passing the pieces through a 10 cm hot zone at 10 mm per minute: 10 minutes in the heat.
Công cụ cần thiết:
Lò ốngGăng tay chịu nhiệt6
6
Magnetise the discs
Magnetise the discs
The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.
Công cụ cần thiết:
Nam châm điện
La bànVật liệu
3- 17.76 gTạm thời
- Tạm thời
- 95.55 gTạm thời
Công cụ yêu cầu
15- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
Bản thiết kế này làm ra
Blueprint liên quan
Các blueprint này chia sẻ kiến thức — kỹ thuật, vật liệu hoặc nguyên tắc
CC0 Phạm vi công cộng
Bản thiết kế này được phát hành theo CC0. Bạn tự do sao chép, sửa đổi, phân phối và sử dụng cho bất kỳ mục đích nào mà không cần xin phép.
Hỗ trợ nhà sáng tạo bằng cách mua sản phẩm qua bản thiết kế, nơi họ nhận Hoa hồng nhà sáng tạo do nhà bán hàng đặt, hoặc tạo phiên bản mới và kết nối trong bản thiết kế riêng để chia sẻ doanh thu.