Barium Ferrite Disc Magnet: 0.5 mol BaCO3 to 3.5 mol Iron Oxide, 10 Minutes at 1330 °C (Went, Philips 1956, Ex. 4)
A barium ferrite with much more iron oxide: 0.5 mol barium carbonate to 3.5 mol, milled 15.5 hours, bound, formed and sintered 10 minutes at 1330 °C. Went's rod held 2,040 gauss with a coercive force of 2,380 oersted.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 4. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Nâng cao
2 days
Hướng dẫn
1
1
Weigh barium carbonate and iron oxide
Weigh barium carbonate and iron oxide
Weigh 99.2 g barium carbonate (0.5 mol) and 564.8 g ferric oxide (3.5 mol). Barium carbonate is poisonous if swallowed: gloves and a dust respirator.
Vật liệu cho bước này:
Bari cacbonat (witherit)99.2 g
Oxit sắt(III)564.8 gCông cụ cần thiết:
Cân hai đĩa
Găng tay cao su
Mặt nạ phòng độc P1002
2
Mill with alcohol 15.5 hours, dry and sieve
Mill with alcohol 15.5 hours, dry and sieve
Grind the mixture with alcohol in a ball mill for 15.5 hours, then dry it and sieve it.
Công cụ cần thiết:
Máy nghiền bi sắt
Etanol phẩm cấp thí nghiệm, 95 %
Lò sấy
Sàng3
3
Knead with a binder and form
Knead with a binder and form
Mix 300 g of the powder with a binder such as polyvinyl alcohol (Went names it or nitrocellulose) into a kneadable mass. The patent extrudes rods about 3 mm across; ours: press discs at 1.5 tonnes per cm², as in its other examples. Dry them in air for about 24 hours.
Công cụ cần thiết:
Bột polyvinyl alcohol
Máy ép thủy lực
Khuôn ép đĩaLò sấy4
4
Sinter in air at 1330 °C for 10 minutes
Sinter in air at 1330 °C for 10 minutes
Sinter the pieces in air at 1330 °C for 10 minutes. The patent gives no zone length or speed for this example.
Công cụ cần thiết:
Lò ống
Găng tay chịu nhiệt5
5
Magnetise the discs
Magnetise the discs
The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.
Công cụ cần thiết:
Nam châm điện
La bànVật liệu
2- 99.2 gTạm thời
- 564.8 gTạm thời
Công cụ yêu cầu
14- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
Bản thiết kế này làm ra
Blueprint liên quan
Các blueprint này chia sẻ kiến thức — kỹ thuật, vật liệu hoặc nguyên tắc
CC0 Phạm vi công cộng
Bản thiết kế này được phát hành theo CC0. Bạn tự do sao chép, sửa đổi, phân phối và sử dụng cho bất kỳ mục đích nào mà không cần xin phép.
Hỗ trợ nhà sáng tạo bằng cách mua sản phẩm qua bản thiết kế, nơi họ nhận Hoa hồng nhà sáng tạo do nhà bán hàng đặt, hoặc tạo phiên bản mới và kết nối trong bản thiết kế riêng để chia sẻ doanh thu.