Barium-Strontium Ferrite Disc Magnet: 0.09 mol BaCO3, 0.21 mol SrCO3, 1300 °C (Went, Philips 1956, Ex. 31)
A ceramic magnet with both barium and strontium: 0.09 mol barium carbonate and 0.21 mol strontium carbonate to 2.7 mol iron oxide, milled as in Example 28, pressed and passed through a 1300 °C furnace in 10 minutes. Went's rod held 1,340 gauss with a coercive force of 2,640 oersted.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 31. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Nâng cao
2 days
Hướng dẫn
1
1
Weigh the carbonates and iron oxide
Weigh the carbonates and iron oxide
Weigh 17.9 g barium carbonate (0.09 mol), 31.0 g strontium carbonate (0.21 mol), 435.5 g ferric oxide (2.7 mol). Barium carbonate is poisonous if swallowed: gloves and a dust respirator.
Vật liệu cho bước này:
Bari cacbonat (witherit)17.9 g
Stronti cacbonat31 g
Oxit sắt(III)435.5 gCông cụ cần thiết:
Cân hai đĩa
Găng tay cao su
Mặt nạ phòng độc P1002
2
Mill with alcohol 15 hours, dry
Mill with alcohol 15 hours, dry
As in Example 28: grind the mixture with alcohol in a ball mill for 15 hours, then dry it.
Công cụ cần thiết:
Máy nghiền bi sắt
Etanol phẩm cấp thí nghiệm, 95 %
Lò sấy3
3
Press the powder
Press the powder
Example 28 moulds a rod without giving the pressure. Ours: press discs at 1.5 tonnes per cm², the pressure of the patent's other examples.
Công cụ cần thiết:
Máy ép thủy lực
Khuôn ép đĩa4
4
Pass through a 1300 °C zone in 10 minutes
Pass through a 1300 °C zone in 10 minutes
Sinter in air at 1300 °C by passing the pieces through a 10 cm hot zone at 10 mm per minute: 10 minutes in the heat.
Công cụ cần thiết:
Lò ống
Găng tay chịu nhiệt5
5
Magnetise the discs
Magnetise the discs
The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.
Công cụ cần thiết:
Nam châm điện
La bànVật liệu
3- 17.9 gTạm thời
- 31 gTạm thời
- 435.5 gTạm thời
Công cụ yêu cầu
12- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
Bản thiết kế này làm ra
Blueprint liên quan
Các blueprint này chia sẻ kiến thức — kỹ thuật, vật liệu hoặc nguyên tắc
CC0 Phạm vi công cộng
Bản thiết kế này được phát hành theo CC0. Bạn tự do sao chép, sửa đổi, phân phối và sử dụng cho bất kỳ mục đích nào mà không cần xin phép.
Hỗ trợ nhà sáng tạo bằng cách mua sản phẩm qua bản thiết kế, nơi họ nhận Hoa hồng nhà sáng tạo do nhà bán hàng đặt, hoặc tạo phiên bản mới và kết nối trong bản thiết kế riêng để chia sẻ doanh thu.