Oriented Barium Ferrite Disc Magnet: Heated to 500 °C Without a Field (Gorter, Philips 1956, Ex. 6)
A ceramic magnet oriented in the die as in Example 4, but heated to 500 °C with no second field before sintering at 1280 °C. In the principal direction it held 3,025 gauss with a coercive force of 1,550 oersted and a (BH)max of 1.58 × 10⁶.
Source: E. W. Gorter, G. W. Rathenau and A. L. Stuyts (Philips), US 2,762,778 (1956), Example 6. They made blocks; disc size is ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Nâng cao
3 days
Hướng dẫn
1
1
Weigh barium carbonate and iron oxide
Weigh barium carbonate and iron oxide
Weigh 450 g barium carbonate and 2000 g ferric oxide. Barium carbonate is poisonous if swallowed: gloves and a dust respirator.
Vật liệu cho bước này:
Bari cacbonat (witherit)450 g
Oxit sắt(III)2000 gCông cụ cần thiết:
Cân hai đĩa
Găng tay cao su
Mặt nạ phòng độc P1002
2
Mill 20 hours under alcohol, dry
Mill 20 hours under alcohol, dry
Grind the mixture in a ball mill under alcohol for 20 hours, then dry it.
Công cụ cần thiết:
Máy nghiền bi sắt
Etanol phẩm cấp thí nghiệm, 95 %
Lò sấy3
3
Pre-fire: through a 1100 °C zone in 10 minutes
Pre-fire: through a 1100 °C zone in 10 minutes
Pass the dry powder at 20 mm per minute through an electric furnace with a 20 cm hot zone at 1100 °C, in air: 10 minutes in the heat. Let it cool.
Công cụ cần thiết:
Lò ống
Chén nung có nắp (sứ)
Găng tay chịu nhiệt4
4
Grind 12 hours with alcohol, dry
Grind 12 hours with alcohol, dry
Pulverise the pre-fired material in a ball mill with alcohol for 12 hours, then dry it. This is the pre-fired powder.
Công cụ cần thiết:
Máy nghiền bi sắtEtanol phẩm cấp thí nghiệm, 95 %Lò sấy5
5
Stir into 8 % polyvinyl acetate in acetone
Stir into 8 % polyvinyl acetate in acetone
Dissolve polyvinyl acetate in acetone to a 8 % solution and stir the pre-fired powder into it, 1 cc of solution per gram of powder. The binder burns off later.
Công cụ cần thiết:
Polyvinyl axetat
AxetonCân hai đĩa6
6
Orient in a 10000 oersted field
Orient in a 10000 oersted field
Put the suspension in a moulding die between the poles of a magnet and apply a first field of 10000 oersted. Remove the binder solution while the field is on (as in Example 4).
Công cụ cần thiết:
Khuôn ép đĩa
Nam châm điện
Máy ép thủy lực7
7
Heat to 500 °C without a field
Heat to 500 °C without a field
Heat the blocks to 500 °C with no magnetic field.
Công cụ cần thiết:
Lò ốngGăng tay chịu nhiệt8
8
Sinter: through a 1280 °C zone in 5 minutes
Sinter: through a 1280 °C zone in 5 minutes
Pass the block at 20 mm per minute through an electric furnace in air at 1280 °C with a 10 cm hot zone: about 5 minutes in the heat.
Công cụ cần thiết:
Lò ốngGăng tay chịu nhiệt9
9
Magnetise in the principal direction
Magnetise in the principal direction
Magnetise the block along the direction of the first field, the principal direction. The patent magnetises it in a field in that direction; ours: an electromagnet. Find the north face with a compass.
Công cụ cần thiết:
Nam châm điện
La bànVật liệu
2- Tạm thời
- 2000 gTạm thời
Công cụ yêu cầu
15- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
Bản thiết kế này làm ra
Blueprint liên quan
Các blueprint này chia sẻ kiến thức — kỹ thuật, vật liệu hoặc nguyên tắc
CC0 Phạm vi công cộng
Bản thiết kế này được phát hành theo CC0. Bạn tự do sao chép, sửa đổi, phân phối và sử dụng cho bất kỳ mục đích nào mà không cần xin phép.
Hỗ trợ nhà sáng tạo bằng cách mua sản phẩm qua bản thiết kế, nơi họ nhận Hoa hồng nhà sáng tạo do nhà bán hàng đặt, hoặc tạo phiên bản mới và kết nối trong bản thiết kế riêng để chia sẻ doanh thu.