Silicone Sealant: Silicone Oil, Diatomaceous Earth and Methyl Triacetoxysilane (Ceyzeriat 1964)
A one-part silicone that stays a paste in a sealed tube and turns to rubber in the open air. The moisture in the air splits the methyl triacetoxysilane, which then ties the hydroxyl ends of the oil together. Louis Ceyzeriat of Rhône-Poulenc made it with diatomaceous earth as the filler; his Example IV paste became an elastic solid in 15 hours.
Source: L. Ceyzeriat (Rhône-Poulenc), US 3,133,891 (1964), Example IV and columns 3–4. His filler was Celite 350; we use raw diatomaceous earth in its place. Picture drawn by Youblob.
Trung cấp
1 day
Hướng dẫn
1
1
Knead the paste
Knead the paste
Knead 200 parts of hydroxyl-ended silicone oil with 80 parts of diatomaceous earth and 1 part of zinc oxide until it is an even paste. All parts are by weight.
Vật liệu cho bước này:
Dầu silicon đầu hydroxyl200 parts
Đất tảo cát80 parts
Bột kẽm oxit1 partsCông cụ cần thiết:
Máy nhào
Cân hai đĩa2
2
Drive out all moisture
Drive out all moisture
If the sealant is to be kept, it must be made dry: a paste with zinc oxide especially needs this. Heat it in the mixer at 50–200 °C, stirring, until every trace of moisture is gone, then let it cool. The patent gives that range, not one temperature or time.
Công cụ cần thiết:
Máy nhào
Bếp điện phẳng
Nhiệt kế3
3
Mix in the silane
Mix in the silane
Add 3 parts of methyl triacetoxysilane for every 100 parts of paste: 8.4 parts for the whole 281 parts (our arithmetic). Keep the air out while you mix.
Vật liệu cho bước này:
Methyltriacetoxysilane8.4 partsCông cụ cần thiết:
Máy nhàoCân hai đĩa4
4
Fill dry containers and seal them
Fill dry containers and seal them
Without letting any water in, fill it into dry containers and seal them airtight. Kept like this it stays usable for many months.
Công cụ cần thiết:
Hộp bảo quản kín khí5
5
Use: it cures in the air
Use: it cures in the air
Spread or press it where it is needed and leave it in the air. Ceyzeriat's paste was an elastic solid after 15 hours. Pressed as a 2 mm sheet it tested 25.6 kg/cm² in tension, 290 % stretch and Shore A 50; after 24 hours, 39 kg/cm², 260 % and Shore A 58.
Công cụ cần thiết:
Xẻng lậtVật liệu
4- 200 partsTạm thời
- 80 partsTạm thời
- 1 partsTạm thời
- 8.4 partsTạm thời
Bản thiết kế này làm ra
Blueprint liên quan
Các blueprint này chia sẻ kiến thức — kỹ thuật, vật liệu hoặc nguyên tắc
Hydroxyl-Ended Silicone Oil: D4 Opened with Potash, Then Water (Ceyzeriat 1964)
bởi Charlie
Công nghiệp
7
0
0
0
0
0
Nguy hiểm
Methyltriacetoxysilane: Methyltrichlorosilane with Acetic Acid, Then Acetic Anhydride
bởi Charlie
Công nghiệp
11
0
0
0
0
0
Zinc Oxide (Pharmacy): Zinc Carbonate Precipitated with Hot Soda, Then Heated
bởi Charlie
Vô cơ
16
0
0
0
0
0
CC0 Phạm vi công cộng
Bản thiết kế này được phát hành theo CC0. Bạn tự do sao chép, sửa đổi, phân phối và sử dụng cho bất kỳ mục đích nào mà không cần xin phép.
Hỗ trợ nhà sáng tạo bằng cách mua sản phẩm qua bản thiết kế, nơi họ nhận Hoa hồng nhà sáng tạo do nhà bán hàng đặt, hoặc tạo phiên bản mới và kết nối trong bản thiết kế riêng để chia sẻ doanh thu.