Strontium Ferrite Disc Magnet: Presintered, 4 Minutes at 1150 °C (Went, Philips 1956, Ex. 25)
A strontium ferrite with more strontium: 0.4 mol strontium carbonate to 0.8 mol iron oxide, milled, presintered at 1000 °C, milled again, pressed and passed through a 1150 °C furnace in 4 minutes. Went's rod held 1,200 gauss with a coercive force of 3,710 oersted.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 25. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Nâng cao
2 days
Hướng dẫn
1
1
Dry the strontium carbonate and weigh
Dry the strontium carbonate and weigh
Dry the strontium carbonate at 100 °C. Weigh 59.05 g of it (0.4 mol) and 127.5 g ferric oxide (0.8 mol).
Vật liệu cho bước này:
Stronti cacbonat59.05 g
Oxit sắt(III)127.5 gCông cụ cần thiết:
Lò sấy
Cân hai đĩa
Mặt nạ phòng độc P1002
2
Mill 7 hours, dry at 110 °C
Mill 7 hours, dry at 110 °C
Grind with alcohol in a ball mill for 7 hours and dry at 110 °C.
Công cụ cần thiết:
Máy nghiền bi sắt
Etanol phẩm cấp thí nghiệm, 95 %Lò sấy3
3
Presinter in air at 1000 °C for 4 hours
Presinter in air at 1000 °C for 4 hours
Fire in air at 1000 °C for 4 hours.
Công cụ cần thiết:
Lò muffle
Chén nung có nắp (sứ)
Kìm gắp nồi nấu kim loại
Găng tay chịu nhiệt4
4
Mill again, dry, press at 1.5 t/cm²
Mill again, dry, press at 1.5 t/cm²
Grind again 7 hours with alcohol, dry at 110 °C and press at 1.5 tonnes per cm² (ours: discs).
Công cụ cần thiết:
Máy nghiền bi sắtEtanol phẩm cấp thí nghiệm, 95 %Lò sấy
Máy ép thủy lực
Khuôn ép đĩa5
5
Pass through a 1150 °C zone in 4 minutes
Pass through a 1150 °C zone in 4 minutes
Sinter at 1150 °C by passing the pieces through a 4 cm hot zone at 10 mm per minute: 4 minutes in the heat.
Công cụ cần thiết:
Lò ốngGăng tay chịu nhiệt6
6
Magnetise the discs
Magnetise the discs
The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.
Công cụ cần thiết:
Nam châm điện
La bànVật liệu
2- 59.05 gTạm thời
- 127.5 gTạm thời
Công cụ yêu cầu
14- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
Bản thiết kế này làm ra
Blueprint liên quan
Các blueprint này chia sẻ kiến thức — kỹ thuật, vật liệu hoặc nguyên tắc
CC0 Phạm vi công cộng
Bản thiết kế này được phát hành theo CC0. Bạn tự do sao chép, sửa đổi, phân phối và sử dụng cho bất kỳ mục đích nào mà không cần xin phép.
Hỗ trợ nhà sáng tạo bằng cách mua sản phẩm qua bản thiết kế, nơi họ nhận Hoa hồng nhà sáng tạo do nhà bán hàng đặt, hoặc tạo phiên bản mới và kết nối trong bản thiết kế riêng để chia sẻ doanh thu.