Strontium Ferrite Disc Magnet, Sintered 4 Hours at 1100 °C (Went, Philips 1956, Ex. 34)
A strontium ferrite magnet made exactly like Went's barium ferrite of Example 34, with strontium carbonate in place of barium carbonate: 29.5 g of it to 191.7 g iron oxide, milled, fired, milled again, pressed and sintered for 4 hours. This iteration sinters at 1100 °C, where his rod held 1,220 gauss with a coercive force of 3,880 oersted.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 34. They pressed rods; the disc size is ours. The patent does not say how to magnetise it; our way is stated. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Nâng cao
2 days
Hướng dẫn
1
1
Weigh strontium carbonate and iron oxide
Weigh strontium carbonate and iron oxide
Weigh 29.5 g of strontium carbonate and 191.7 g of ferric oxide, Fe2O3. The patent makes this second mixture "in exactly the same manner" as the barium one.
Vật liệu cho bước này:
Stronti cacbonat29.5 g
Oxit sắt(III)191.7 gCông cụ cần thiết:
Cân hai đĩa
Găng tay cao su
Mặt nạ phòng độc P1002
2
Mill with ethanol for 4 hours
Mill with ethanol for 4 hours
Grind the mixture with ethanol in an iron ball mill for 4 hours. Let the ethanol evaporate, then dry the powder in a drying oven.
Công cụ cần thiết:
Máy nghiền bi sắt
Etanol phẩm cấp thí nghiệm, 95 %
Lò sấy3
3
Presinter at 1000 °C for 4 hours
Presinter at 1000 °C for 4 hours
Fire the dry powder in air at 1000 °C for 4 hours (ours: in a lidded porcelain crucible in a muffle furnace). Let it cool.
Công cụ cần thiết:
Lò muffle
Chén nung có nắp (sứ)
Kìm gắp nồi nấu kim loại
Găng tay chịu nhiệt4
4
Mill again for 4 hours
Mill again for 4 hours
Grind the presintered product with ethanol in the ball mill for another 4 hours. Let the ethanol evaporate.
Công cụ cần thiết:
Máy nghiền bi sắtEtanol phẩm cấp thí nghiệm, 95 %Lò sấyMặt nạ phòng độc P1005
5
Press discs at 1.5 tons per cm²
Press discs at 1.5 tons per cm²
Press the powder at 1.5 tons/cm². The patent pressed rods; we press discs. Ours: a die 20 mm across, so about 4.7 tonnes on the punch (our arithmetic: 1.5 × 3.14 cm²).
Công cụ cần thiết:
Máy ép thủy lực
Khuôn ép đĩa6
6
Sinter 4 hours at 1100 °C
Sinter 4 hours at 1100 °C
Sinter the discs for 4 hours at 1100 °C in oxygen or in air. The patent's strontium rod at 1100 °C: 1,220 gauss and 3,880 oersted.
Công cụ cần thiết:
Lò muffleKìm gắp nồi nấu kim loạiGăng tay chịu nhiệt7
7
Magnetise the discs
Magnetise the discs
The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.
Công cụ cần thiết:
Nam châm điện
La bànVật liệu
2- 29.5 gTạm thời
- 191.7 gTạm thời
Công cụ yêu cầu
14- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
- Tạm thời
Bản thiết kế này làm ra
Blueprint liên quan
Các blueprint này chia sẻ kiến thức — kỹ thuật, vật liệu hoặc nguyên tắc
Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)
bởi Charlie
Công nghiệp
2
0
0
0
0
0
Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)
bởi Charlie
Công nghiệp
6
0
0
0
0
0
Nguy hiểm
Ferrite Toroid Core: Nickel-Zinc Ferrite Sintered at 1300 °C in Oxygen (Snoek)
bởi Charlie
Công nghiệp
15
0
0
0
0
0
Ferric Oxide: Hydroxide Precipitated from Ferric Chloride with Ammonia, Then Heated
bởi Charlie
Vô cơ
11
0
0
0
0
0
CC0 Phạm vi công cộng
Bản thiết kế này được phát hành theo CC0. Bạn tự do sao chép, sửa đổi, phân phối và sử dụng cho bất kỳ mục đích nào mà không cần xin phép.
Hỗ trợ nhà sáng tạo bằng cách mua sản phẩm qua bản thiết kế, nơi họ nhận Hoa hồng nhà sáng tạo do nhà bán hàng đặt, hoặc tạo phiên bản mới và kết nối trong bản thiết kế riêng để chia sẻ doanh thu.