Barium-Strontium Ferrite Disc Magnet: 0.5 mol BaCO3, 0.5 mol SrCO3, 1260 °C (Went, Philips 1956, Ex. 28)
Omegatron (Wikimedia Commons) · CC BY-SA 3.0
Charlie

Créé par

Charlie

28. octobre 2026DE
1
0
0
0
0

Barium-Strontium Ferrite Disc Magnet: 0.5 mol BaCO3, 0.5 mol SrCO3, 1260 °C (Went, Philips 1956, Ex. 28)

A ceramic magnet with both barium and strontium: 0.5 mol barium carbonate and 0.5 mol strontium carbonate to 3 mol iron oxide, milled 15 hours, pressed and passed through a 1260 °C furnace in 20 minutes. Went's rod held 1,665 gauss with a coercive force of 3,235 oersted. Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 28. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Avancé
2 days

Consignes

1

Weigh the carbonates and iron oxide

Weigh 99.2 g barium carbonate (0.5 mol), 73.8 g strontium carbonate (0.5 mol), 483.3 g ferric oxide (3 mol). Barium carbonate is poisonous if swallowed: gloves and a dust respirator.

Matériaux pour cette étape :

Carbonate de baryum (withérite)Carbonate de baryum (withérite)99.2 g
Carbonate de strontiumCarbonate de strontium73.8 g
Oxyde ferriqueOxyde ferrique483.3 g

Outils nécessaires :

Balance à fléauBalance à fléau
Gants en caoutchoucGants en caoutchouc
Masque respiratoire P100Masque respiratoire P100
2

Mill with alcohol 15 hours, dry

Grind the mixture with alcohol in a ball mill for 15 hours, then dry it.

Outils nécessaires :

Broyeur à boulets de ferBroyeur à boulets de fer
Éthanol de laboratoire, 95 %Éthanol de laboratoire, 95 %
Étuve de séchageÉtuve de séchage
3

Press the powder

Example 28 moulds a rod without giving the pressure. Ours: press discs at 1.5 tonnes per cm², the pressure of the patent's other examples.

Outils nécessaires :

Presse hydrauliquePresse hydraulique
Matrice de pressage de disquesMatrice de pressage de disques
4

Pass through a 1260 °C zone in 20 minutes

Sinter at 1260 °C by passing the pieces through a 10 cm hot zone at 5 mm per minute: 20 minutes in the heat.

Outils nécessaires :

Four tubulaireFour tubulaire
Gants résistants à la chaleurGants résistants à la chaleur
5

Magnetise the discs

The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.

Outils nécessaires :

ÉlectroaimantÉlectroaimant
BoussoleBoussole

Matériaux

3

Outils requis

12

Ce plan fabrique

Thumbnail
Espace réservé

Aimant disque

Free

2
0
1

Blueprints liés

Ces blueprints partagent des connaissances — techniques, matériaux ou principes

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

par CharlieDE

Industriel

1
0
0
0
0
0
Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

par CharlieDE

Industriel

4
0
0
0
0
0

CC0 Domaine public

Ce blueprint est publié sous CC0. Vous êtes libre de copier, modifier, distribuer et utiliser ce travail pour tout usage, sans demander la permission.

Soutenez le Maker en achetant des produits via son Blueprint où il perçoit une Commission Maker définie par les Vendeurs, ou créez une nouvelle itération de ce Blueprint et incluez-le comme connexion dans votre propre Blueprint pour partager les revenus.

Commentaires

(0)

Se connecter pour participer à la discussion

Chargement des commentaires...