Strontium Ferrite Disc Magnet: Presintered at 1100 °C, 0.2 mol SrCO3 to 1.1 mol Iron Oxide (Went, Philips 1956, Ex. 7)
A strontium ferrite: 0.2 mol strontium carbonate to 1.1 mol iron oxide, dried, milled, presintered 3.5 hours at 1100 °C, bound, formed and passed through a 1280 °C furnace in 10 minutes. Went's rod held 2,155 gauss with a coercive force of 2,500 oersted.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 7. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Avancé
2 days
Consignes
1
1
Weigh strontium carbonate and iron oxide
Weigh strontium carbonate and iron oxide
Weigh 29.5 g strontium carbonate (0.2 mol) and 176.1 g ferric oxide (1.1 mol).
Matériaux pour cette étape :
Carbonate de strontium29.5 g
Oxyde ferrique176.1 gOutils nécessaires :
Balance à fléau
Masque respiratoire P1002
2
Dry at 200 °C, mill with alcohol 4 hours
Dry at 200 °C, mill with alcohol 4 hours
Dry the mixture at 200 °C, then grind it with alcohol in a ball mill for 4 hours and dry it.
Outils nécessaires :
Étuve de séchage
Broyeur à boulets de fer
Éthanol de laboratoire, 95 %3
3
Presinter in air at 1100 °C for 3.5 hours
Presinter in air at 1100 °C for 3.5 hours
Fire the powder in air at 1100 °C for about 3.5 hours.
Outils nécessaires :
Four à moufle
Creuset avec couvercle (porcelaine)
Pince à creuset
Gants résistants à la chaleur4
4
Add a binder and form, dry overnight
Add a binder and form, dry overnight
Add a binder as in Example 1 (polyvinyl alcohol or nitrocellulose). The patent extrudes rods; ours: press discs at 1.5 tonnes per cm². Dry overnight.
Outils nécessaires :
Alcool polyvinylique en poudre
Presse hydraulique
Matrice de pressage de disquesÉtuve de séchage5
5
Pass through a 1280 °C zone in 10 minutes
Pass through a 1280 °C zone in 10 minutes
Sinter in air at 1280 °C by passing the pieces through a 10 cm hot zone at 10 mm per minute: 10 minutes in the heat.
Outils nécessaires :
Four tubulaireGants résistants à la chaleur6
6
Magnetise the discs
Magnetise the discs
The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.
Outils nécessaires :
Électroaimant
BoussoleMatériaux
2- 29.5 gEspace réservé
- 176.1 gEspace réservé
Outils requis
15- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
Ce plan fabrique
Blueprints liés
Ces blueprints partagent des connaissances — techniques, matériaux ou principes
CC0 Domaine public
Ce blueprint est publié sous CC0. Vous êtes libre de copier, modifier, distribuer et utiliser ce travail pour tout usage, sans demander la permission.
Soutenez le Maker en achetant des produits via son Blueprint où il perçoit une Commission Maker définie par les Vendeurs, ou créez une nouvelle itération de ce Blueprint et incluez-le comme connexion dans votre propre Blueprint pour partager les revenus.