Strontium Ferrite Disc Magnet: 1 mol SrCO3 to 2.5 mol Iron Oxide, 1200 °C (Went, Philips 1956, Ex. 9)
A strontium ferrite: 1 mol strontium carbonate to 2.5 mol iron oxide, milled, bound and formed as in Example 4, and passed through a 1200 °C furnace in 3 to 5 minutes. Went's rod held 1,555 gauss with a coercive force of 3,160 oersted.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 9. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Avancé
2 days
Consignes
1
1
Weigh strontium carbonate and iron oxide
Weigh strontium carbonate and iron oxide
Weigh 147.6 g strontium carbonate (1 mol) and 403.4 g ferric oxide (2.5 mol).
Matériaux pour cette étape :
Carbonate de strontium147.6 g
Oxyde ferrique403.4 gOutils nécessaires :
Balance à fléau
Masque respiratoire P1002
2
Mill with alcohol 15.5 hours, dry and sieve
Mill with alcohol 15.5 hours, dry and sieve
As in Example 4: grind the mixture with alcohol in a ball mill for 15.5 hours, then dry it and sieve it.
Outils nécessaires :
Broyeur à boulets de fer
Éthanol de laboratoire, 95 %
Étuve de séchage
Crible3
3
Knead with a binder and form
Knead with a binder and form
Mix 300 g of the powder with a binder such as polyvinyl alcohol (Went names it or nitrocellulose) into a kneadable mass. The patent extrudes rods about 3 mm across; ours: press discs at 1.5 tonnes per cm², as in its other examples. Dry them in air for about 24 hours.
Outils nécessaires :
Alcool polyvinylique en poudre
Presse hydraulique
Matrice de pressage de disquesÉtuve de séchage4
4
Pass through a 1200 °C zone in 3 to 5 minutes
Pass through a 1200 °C zone in 3 to 5 minutes
Sinter in air at 1200 °C by passing the pieces through a 3 to 5 cm hot zone at 10 mm per minute: 3 to 5 minutes in the heat.
Outils nécessaires :
Four tubulaire
Gants résistants à la chaleur5
5
Magnetise the discs
Magnetise the discs
The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.
Outils nécessaires :
Électroaimant
BoussoleMatériaux
2- 147.6 gEspace réservé
- 403.4 gEspace réservé
Outils requis
13- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
Ce plan fabrique
Blueprints liés
Ces blueprints partagent des connaissances — techniques, matériaux ou principes