PTFE Disc: Sintered in a Molten Nitrate Bath, Cooled Slowly (Brubaker & Hanford 1946)
A PTFE disc pressed cold, then sintered by dipping it in molten salt at 380 °C for half an hour. Instead of being quenched, it cools slowly between magnesite blocks. The patent says slowly cooled pieces are a little softer and less stiff, which is often better for machining.
Source: M. M. Brubaker and W. E. Hanford (du Pont), US 2,400,099 (1946), Example II. The patent gives no nitrate-to-nitrite ratio. The mould, press, pot and burner are ours. Picture drawn by Youblob.
上級者
1 day
手順
1
1
Press a disc at 500 psi
Press a disc at 500 psi
At 25 °C, press PTFE powder at 500 lb/sq in into a disc 2 in across and ⅜ in thick.
このステップの材料:
PTFE 樹脂粉末1 as required for the disc必要な工具:
圧縮成形金型
油圧プレス
定規2
2
Melt the salt bath at 380 °C
Melt the salt bath at 380 °C
Melt a mixture of sodium nitrate and sodium nitrite and hold it at 380 °C. The patent gives no ratio. Ours: a cast iron pot on a gas burner.
必要な工具:
チリ硝石（硝酸ナトリウム）
亜硝酸ナトリウム
鋳鉄の鍋
ガスバーナー
表示器付き熱電対3
3
Dip the disc for half an hour
Dip the disc for half an hour
Lower the pressed disc into the molten bath and leave it there for ½ hour.
必要な工具:
火ばさみ鋳鉄の鍋表示器付き熱電対4
4
Cool it slowly between magnesite blocks
Cool it slowly between magnesite blocks
Take the disc out and lay it between two magnesite blocks so it cools to room temperature over 1 hour. It comes out tough and even, close to its pressed shape.
必要な工具:
火ばさみ
マグネサイトブロックこの設計図で作るもの
関連ブループリント
これらのブループリントは知識を共有しています — 技術、材料、原理
CC0 パブリックドメイン
このブループリントはCC0で公開されています。許可を求めずに、自由にコピー、修正、配布、あらゆる目的で使用できます。
メイカーを応援するには、ブループリント経由で製品を購入してください。メイカーには メイカーコミッション がベンダーにより設定されています。または、このブループリントの新しいイテレーションを作成し、自分のブループリントにコネクションとして含めて収益を共有できます。