Barium Ferrite Disc Magnet from Natural Magnetite, Presintered at 900 °C (Went, Philips 1956, Ex. 36, Procedure 1)
A barium ferrite magnet made from natural magnetite instead of ferric oxide: barium carbonate and magnetite ground 18 hours, presintered 3 hours at 900 °C, ground again 18 hours, pressed and sintered 2 hours at 1200 °C. Went's rod held 1,450 gauss with a coercive force of 2,425 oersted.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 36. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
उन्नत
2 days
निर्देशनहरू
1
1
Weigh barium carbonate and magnetite
Weigh barium carbonate and magnetite
Weigh 9.9 g barium carbonate (0.05 mol) and 46.9 g natural magnetite, Fe3O4 (0.20 mol). Barium carbonate is poisonous if swallowed: gloves and a dust respirator.
यस चरणका सामग्री:
ब्यारियम कार्बोनेट (विथराइट)9.9 ग्राम
म्याग्नेटाइट46.9 ग्रामचाहिने औजार:
समभुज तराजु
रबरका पन्जा
P100 स्वास रक्षक2
2
Grind 18 hours in a ball mill
Grind 18 hours in a ball mill
Grind the mixture in a ball mill for 18 hours. The patent does not say whether wet or dry.
चाहिने औजार:
फलामे बल मिलP100 स्वास रक्षक3
3
Presinter at 900 °C for 3 hours
Presinter at 900 °C for 3 hours
Fire the ground mixture at 900 °C for three hours and let it cool.
चाहिने औजार:
मफल भट्टी
बिर्कोसहितको क्रुसिबल (चिनियाँ माटो)
मुसाको चिम्टा
ताप सहने पन्जा4
4
Grind 18 hours in a ball mill
Grind 18 hours in a ball mill
Grind it again in a ball mill for 18 hours. The patent does not say whether wet or dry.
चाहिने औजार:
फलामे बल मिलP100 स्वास रक्षक5
5
Press at 1.5 t/cm²
Press at 1.5 t/cm²
Press at 1.5 tonnes per cm² (ours: discs instead of a rod).
चाहिने औजार:
हाइड्रोलिक प्रेस
डिस्क थिच्ने डाइ6
6
Sinter at 1200 °C for 2 hours
Sinter at 1200 °C for 2 hours
Sinter at 1200 °C for 2 hours. The patent gives no atmosphere for this example. Went's rod: 1,450 gauss, 2,425 oersted.
चाहिने औजार:
मफल भट्टीमुसाको चिम्टाताप सहने पन्जा7
7
Magnetise the discs
Magnetise the discs
The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.
चाहिने औजार:
विद्युत् चुम्बक
दिशासूचक यन्त्रसामग्री
2- 9.9 ग्रामप्लेसहोल्डर
- 46.9 ग्रामप्लेसहोल्डर
आवश्यक उपकरणहरू
12- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
यो खाकाले बनाउँछ
सम्बन्धित ब्लुप्रिन्ट
यी ब्लुप्रिन्टहरूले ज्ञान साझा गर्छन् — प्रविधि, सामग्री वा सिद्धान्त
CC0 सार्वजनिक डोमेन
यो ब्लुप्रिन्ट CC0 अन्तर्गत जारी गरिएको छ। तपाईं अनुमति नसोधी प्रतिलिपि, परिमार्जन, वितरण र प्रयोग गर्न सक्नुहुन्छ।
ब्लुप्रिन्ट मार्फत उत्पादनहरू किनेर सिर्जनाकर्तालाई सहयोग गर्नुहोस् सिर्जनाकर्ता कमिसन विक्रेताले तोकेको, वा यो ब्लुप्रिन्टको नयाँ संस्करण बनाउनुहोस् र आम्दानी बाँड्न आफ्नो ब्लुप्रिन्टमा जडानको रूपमा समावेश गर्नुहोस्।