Bone Ash by Calcining Bones
Bone ash is the white material left when bones are calcined: mainly calcium phosphate, generally given as Ca5(OH)(PO4)3, about 56% calcium oxide and 42% phosphorus pentoxide by analysis. It melts only at about 1670 °C. Its porous, high-melting structure makes it the classic cupel for separating silver and gold from lead, and it forms about half of the body of bone china.
शुरुआती
Workshop process
निर्देशनहरू
1
1
Clean the bones
Clean the bones
Remove any meat from the bones, then degrease them.
यस चरणका सामग्री:
हाड1 as requiredचाहिने औजार:
चक्कु2
2
Calcine
Calcine
Calcine the bones in a kiln. For bone china they are calcined to around 1000 °C (up to about 1100 °C), which removes all organic matter and leaves the bone sterilised and white; traditional bone ash was calcined lower, at around 800 °C. Most bones keep their cellular structure through calcination. Handle the hot bones with tongs and heat-resistant gloves, and let them cool before grinding.
चाहिने औजार:
भट्टी
चिम्टा
ताप सहने पन्जा3
3
Grind
Grind
Grind the calcined bone with water to a fine particle size, then partially dewater it.
यस चरणका सामग्री:
पानी1 as requiredचाहिने औजार:
खल र लोहोरोयो खाकाले बनाउँछ
सम्बन्धित ब्लुप्रिन्ट
यी ब्लुप्रिन्टहरूले ज्ञान साझा गर्छन् — प्रविधि, सामग्री वा सिद्धान्त
CC0 सार्वजनिक डोमेन
यो ब्लुप्रिन्ट CC0 अन्तर्गत जारी गरिएको छ। तपाईं अनुमति नसोधी प्रतिलिपि, परिमार्जन, वितरण र प्रयोग गर्न सक्नुहुन्छ।
ब्लुप्रिन्ट मार्फत उत्पादनहरू किनेर सिर्जनाकर्तालाई सहयोग गर्नुहोस् सिर्जनाकर्ता कमिसन विक्रेताले तोकेको, वा यो ब्लुप्रिन्टको नयाँ संस्करण बनाउनुहोस् र आम्दानी बाँड्न आफ्नो ब्लुप्रिन्टमा जडानको रूपमा समावेश गर्नुहोस्।