Strontium Ferrite Disc Magnet: Example 9 Without the Orienting Field (Gorter, Philips 1956, Ex. 9 Comparison)
Made as in Example 9 but without the first, orienting field. Gorter's comparison blocks held 2,075 gauss with a coercive force of 3,225 oersted and a (BH)max of 0.88 × 10⁶.
Source: E. W. Gorter, G. W. Rathenau and A. L. Stuyts (Philips), US 2,762,778 (1956), Example 9. They made blocks; disc size is ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
उन्नत
3 days
निर्देशनहरू
1
1
Weigh strontium carbonate and iron oxide
Weigh strontium carbonate and iron oxide
Weigh 29.5 g strontium carbonate and 163 g ferric oxide.
यस चरणका सामग्री:
स्ट्रन्सियम कार्बोनेट29.5 ग्राम
फेरिक अक्साइड163 ग्रामचाहिने औजार:
समभुज तराजु
P100 स्वास रक्षक2
2
Mill 15 hours with alcohol, dry
Mill 15 hours with alcohol, dry
Grind in a ball mill with alcohol for 15 hours. Remove the alcohol and dry the powder.
चाहिने औजार:
फलामे बल मिल
इथानोल - प्रयोगशाला श्रेणी, 95 %
सुकाउने भट्टी3
3
Pre-fire 2 hours at 1000 °C in air
Pre-fire 2 hours at 1000 °C in air
Heat the powder for 2 hours at 1000 °C in an electric furnace in air. Let it cool.
चाहिने औजार:
मफल भट्टी
बिर्कोसहितको क्रुसिबल (चिनियाँ माटो)
मुसाको चिम्टा
ताप सहने पन्जा4
4
Grind 4 hours in an agate centrifugal mill
Grind 4 hours in an agate centrifugal mill
Grind the cooled material for 4 hours with alcohol in an agate centrifugal mill, then dry it. This is the pre-fired powder. Example 9 does not say how its powder was pre-fired; ours: as in Example 8.
चाहिने औजार:
अकीक अपकेन्द्री मिलइथानोल - प्रयोगशाला श्रेणी, 95 %सुकाउने भट्टी5
5
Stir into 8 % polyvinyl acetate in acetone
Stir into 8 % polyvinyl acetate in acetone
Dissolve polyvinyl acetate in acetone to a 8 % solution and stir the pre-fired powder into it, 1 cc of solution per gram of powder. The binder burns off later.
चाहिने औजार:
पोलिभिनाइल एसिटेट
एसिटोनसमभुज तराजु6
6
Mould without a first field
Mould without a first field
Put the suspension in a moulding die and remove the binder solution without any magnetic field. This is the patent's comparison block.
चाहिने औजार:
डिस्क थिच्ने डाइ
हाइड्रोलिक प्रेस7
7
Heat to 500 °C in a 2000 oersted field
Heat to 500 °C in a 2000 oersted field
Put the block in an electric furnace between the magnet's poles. With a second field of 2000 oersted along the first field's direction, heat to 500 °C, which burns off the rest of the binder. Then switch the field off.
चाहिने औजार:
ट्युब फर्नेस
विद्युत् चुम्बकताप सहने पन्जा8
8
Sinter: through a 1280 °C zone in 5 minutes
Sinter: through a 1280 °C zone in 5 minutes
Pass the block at 20 mm per minute through an electric furnace in air at 1280 °C with a 10 cm hot zone: about 5 minutes in the heat.
चाहिने औजार:
ट्युब फर्नेसताप सहने पन्जा9
9
Magnetise the block
Magnetise the block
Magnetise the block in a field. Without the orienting field it has no preferred direction. Ours: an electromagnet. Find the north face with a compass.
चाहिने औजार:
विद्युत् चुम्बक
दिशासूचक यन्त्रसामग्री
2- 29.5 ग्रामप्लेसहोल्डर
- 163 ग्रामप्लेसहोल्डर
आवश्यक उपकरणहरू
17- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
यो खाकाले बनाउँछ
सम्बन्धित ब्लुप्रिन्ट
यी ब्लुप्रिन्टहरूले ज्ञान साझा गर्छन् — प्रविधि, सामग्री वा सिद्धान्त
CC0 सार्वजनिक डोमेन
यो ब्लुप्रिन्ट CC0 अन्तर्गत जारी गरिएको छ। तपाईं अनुमति नसोधी प्रतिलिपि, परिमार्जन, वितरण र प्रयोग गर्न सक्नुहुन्छ।
ब्लुप्रिन्ट मार्फत उत्पादनहरू किनेर सिर्जनाकर्तालाई सहयोग गर्नुहोस् सिर्जनाकर्ता कमिसन विक्रेताले तोकेको, वा यो ब्लुप्रिन्टको नयाँ संस्करण बनाउनुहोस् र आम्दानी बाँड्न आफ्नो ब्लुप्रिन्टमा जडानको रूपमा समावेश गर्नुहोस्।