Strontium Ferrite Disc Magnet: Presintered at 1100 °C, 0.1 mol SrCO3 to 0.7 mol Iron Oxide (Went, Philips 1956, Ex. 8)
A strontium ferrite: 0.1 mol strontium carbonate to 0.7 mol iron oxide, dried, milled, presintered 3.5 hours at 1100 °C, bound, formed and passed through a 1280 °C furnace in 10 minutes. Went's rod held 1,535 gauss with a coercive force of 2,800 oersted.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 8. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
उन्नत
2 days
निर्देशनहरू
1
1
Weigh strontium carbonate and iron oxide
Weigh strontium carbonate and iron oxide
Weigh 14.8 g strontium carbonate (0.1 mol) and 112.1 g ferric oxide (0.7 mol).
यस चरणका सामग्री:
स्ट्रन्सियम कार्बोनेट14.8 ग्राम
फेरिक अक्साइड112.1 ग्रामचाहिने औजार:
समभुज तराजु
P100 स्वास रक्षक2
2
Dry at 200 °C, mill with alcohol 4 hours
Dry at 200 °C, mill with alcohol 4 hours
Dry the mixture at 200 °C, then grind it with alcohol in a ball mill for 4 hours and dry it.
चाहिने औजार:
सुकाउने भट्टी
फलामे बल मिल
इथानोल - प्रयोगशाला श्रेणी, 95 %3
3
Presinter in air at 1100 °C for 3.5 hours
Presinter in air at 1100 °C for 3.5 hours
Fire the powder in air at 1100 °C for about 3.5 hours.
चाहिने औजार:
मफल भट्टी
बिर्कोसहितको क्रुसिबल (चिनियाँ माटो)
मुसाको चिम्टा
ताप सहने पन्जा4
4
Add a binder and form, dry overnight
Add a binder and form, dry overnight
Add a binder as in Example 1 (polyvinyl alcohol or nitrocellulose). The patent extrudes rods; ours: press discs at 1.5 tonnes per cm². Dry overnight.
चाहिने औजार:
पोलिभिनाइल अल्कोहल धुलो
हाइड्रोलिक प्रेस
डिस्क थिच्ने डाइसुकाउने भट्टी5
5
Pass through a 1280 °C zone in 10 minutes
Pass through a 1280 °C zone in 10 minutes
Sinter in air at 1280 °C by passing the pieces through a 10 cm hot zone at 10 mm per minute: 10 minutes in the heat.
चाहिने औजार:
ट्युब फर्नेसताप सहने पन्जा6
6
Magnetise the discs
Magnetise the discs
The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.
चाहिने औजार:
विद्युत् चुम्बक
दिशासूचक यन्त्रसामग्री
2- 14.8 ग्रामप्लेसहोल्डर
- 112.1 ग्रामप्लेसहोल्डर
आवश्यक उपकरणहरू
15- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
यो खाकाले बनाउँछ
सम्बन्धित ब्लुप्रिन्ट
यी ब्लुप्रिन्टहरूले ज्ञान साझा गर्छन् — प्रविधि, सामग्री वा सिद्धान्त
CC0 सार्वजनिक डोमेन
यो ब्लुप्रिन्ट CC0 अन्तर्गत जारी गरिएको छ। तपाईं अनुमति नसोधी प्रतिलिपि, परिमार्जन, वितरण र प्रयोग गर्न सक्नुहुन्छ।
ब्लुप्रिन्ट मार्फत उत्पादनहरू किनेर सिर्जनाकर्तालाई सहयोग गर्नुहोस् सिर्जनाकर्ता कमिसन विक्रेताले तोकेको, वा यो ब्लुप्रिन्टको नयाँ संस्करण बनाउनुहोस् र आम्दानी बाँड्न आफ्नो ब्लुप्रिन्टमा जडानको रूपमा समावेश गर्नुहोस्।