Bearing Steel Bar (52100): Crucible Steel Alloyed with Chromium
52100 is the steel of ball bearings: about 1 % carbon and 1.5 % chromium (ASM). The standard, ASTM A295, allows 0.93–1.05 % carbon and 1.35–1.60 % chromium. Here crucible steel is melted with chromium and a little manganese, cast, forged to bar and annealed soft for working.
Our method, not the factory one: factory 52100 is melted in an electric furnace and vacuum-degassed to meet the standard's limits on inclusions. A crucible melt can reach the composition, but only a lab test shows whether it is clean enough for bearings.
The picture: our drawing, crucible to bar.
İleri
2 days
Talimatlar
1
1
Weigh the charge
Weigh the charge
For 1 kg: 981.5 g crucible steel of about 1 % carbon, 15 g chromium and 3.5 g manganese (our figures; see the last step). Use steel whose analysis you know.
Bu adım için malzemeler:
Pota çeliği981.5 g
Krom Metali15 g
Mangan3.5 gGerekli aletler:
Dijital Mutfak Terazisi2
2
Melt
Melt
Pack the steel, chromium and manganese in a covered clay crucible and melt it in the furnace. The alloy is fully liquid above 1450 °C.
Gerekli aletler:
Derin Kil Pota
Tuğla fırın
Körük
Kaynak eldivenleri
Deri Önlük
Koruyucu gözlük3
3
Cast the ingot
Cast the ingot
Lift the crucible out with tongs and pour into a cast-iron ingot mould. Let it cool.
Gerekli aletler:
Pota Maşası
Külçe kalıbıKaynak eldivenleriDeri ÖnlükKoruyucu gözlük4
4
Forge to bar
Forge to bar
Heat the ingot to a cherry-red heat and no hotter, and draw it out on the anvil to a round or square bar. Reheat when the colour drops; never hammer it cold.
Bu adım için malzemeler:
Odun Kömürü1 as requiredGerekli aletler:
Demirci ocağı
Örs
Balyoz
Enine keski başlı çekiç
Demirci kerpeteni
Dijital Kumpas 6 İnçKaynak eldivenleriDeri ÖnlükKoruyucu gözlük5
5
Test the analysis
Test the analysis
Drill clean chips from the bar and have a lab analyse carbon, chromium, manganese, silicon, phosphorus and sulphur. Keep the bar only if it is within 52100 limits.
Gerekli aletler:
El matkabı
Kapaklı Cam KavanozlarKoruyucu gözlük6
6
Anneal soft
Anneal soft
In the oven, hold the bar at 793 °C (1460 °F) for 30 minutes, cool in the oven no faster than 500 °C an hour to 682 °C (1260 °F), then cool in air (Verhoeven's anneal).
Gerekli aletler:
Isıl işlem fırını
Göstergeli ısıl çiftDemirci kerpeteniKaynak eldivenleri7
7
The charge
The charge
Jupyter defteri yükleniyor…
Malzemeler
4- 981.5 gYer Tutucu
- 15 gYer Tutucu
- 3.5 gYer Tutucu
- 1 as requiredYer Tutucu
Gerekli Aletler
19- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
Bu planla yapılan
İlgili Blueprint'ler
Bu blueprint'ler bilgi paylaşır — teknikler, malzemeler veya ilkeler
Crucible Cast Steel by the Huntsman Process — Remelting Blister Steel into Flawless Ingots
Tarkin tarafından
Metal işleme
49
0
0
0
0
0
Chromium Metal: Chromic Oxide Reduced by Aluminium (Thermit)
Forge tarafından
Metal işleme
17
0
0
0
0
0
Tool-Steel Bar: Crucible Steel Drawn Out at a Cherry-Red Heat
Forge tarafından
Demirci
25
0
0
0
0
0
CC0 Kamu Malı
Bu plan CC0 lisansıyla yayınlanmıştır. İzin almadan kopyalayabilir, değiştirebilir, dağıtabilir ve herhangi bir amaçla kullanabilirsiniz.
Planı üzerinden ürün satın alarak Maker'ı destekleyin, böylece Maker Komisyonu Satıcılar tarafından belirlenen komisyonu kazanırlar veya bu Planın yeni bir versiyonunu oluşturun ve gelir paylaşımı için kendi Planınıza bağlantı olarak ekleyin.