Metal Oxide Varistor: Zinc Oxide with 0.5 % Chromic Oxide, Bismuth-Manganese Oxide Paste Fired On (Masuyama 1972, Ex. 7)
A varistor whose bismuth oxide and manganese dioxide are both fired on from a paste: 99.5 % zinc oxide with 0.5 % chromic oxide by moles, sintered at 1350 °C, coated with a 70 : 30 bismuth oxide and manganese dioxide paste and fired at 800 °C. The disc measured a C-value of 167 at 1 mA and a nonlinearity exponent n of 34.2.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 7. Unknown: how the aluminium is sprayed on, what the silver paint is, and how strong the epoxy solution of the paste is. The 10 g batch is our arithmetic. Picture: the patent's drawing.
İleri
2 days
Talimatlar
1
1
Weigh 99.5 : 0.5 and wet-mill 5 hours
Weigh 99.5 : 0.5 and wet-mill 5 hours
Mix zinc oxide and chromic oxide 99.5 : 0.5 by moles. Ours, for 10 g: 9.907 g zinc oxide, 0.093 g chromic oxide (our arithmetic). Mill wet for 5 hours, then dry, as in Example 1. Unknown: the milling liquid.
Bu adım için malzemeler:
Çinko Oksit Tozu9.907 g
Krom Oksit0.093 gGerekli aletler:
Eşit kollu terazi
Demir Bilyalı Değirmen
Kurutma fırını2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press discs 13 mm across and 2.5 mm thick at 340 kg/cm², as in Example 1.
Gerekli aletler:
Hidrolik pres
Disk presleme kalıbı
Kumpas3
3
Sinter 1 hour at 1350 °C and furnace-cool
Sinter 1 hour at 1350 °C and furnace-cool
Sinter in air at 1350 °C for 1 hour and let the discs cool in the furnace.
Gerekli aletler:
Mufla fırın4
4
Lap both faces
Lap both faces
Lap both faces with silicon carbide abrasive. Example 7 gives no thickness.
Gerekli aletler:
Silisyum karbür tanesiKumpas5
5
Coat with bismuth and manganese oxide paste, fire at 800 °C
Coat with bismuth and manganese oxide paste, fire at 800 °C
Coat both lapped faces with a paste whose solids are 70 % bismuth oxide and 30 % manganese dioxide by weight, and fire it in air at 800 °C for 30 minutes. Example 7 does not name the paste's liquid; ours: the epoxy-resin butyl-alcohol solution of Example 4. Not given: how much paste.
Bu adım için malzemeler:
Bizmut oksit1 as required
Manganez dioksit (pirolusit)1 as requiredGerekli aletler:
Epoksi reçine
n-ButanolMufla fırın6
6
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint, as in Example 1. Unknown: the spraying method and the paint.
Bu adım için malzemeler:
Alüminyum külçe1 as required
Gümüş iletken boya1 as required
Bakır Tel2 adetGerekli aletler:
Bilinmeyen metal püskürtme yöntemiKumpasMalzemeler
7- 9.907 gYer Tutucu
- 0.093 gYer Tutucu
- 1 as requiredYer Tutucu
- 1 as requiredYer Tutucu
- 1 as requiredYer Tutucu
- 1 as requiredYer Tutucu
- 2 adetYer Tutucu
Gerekli Aletler
11- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
- Yer Tutucu
Bu planla yapılan
İlgili Blueprint'ler
Bu blueprint'ler bilgi paylaşır — teknikler, malzemeler veya ilkeler
CC0 Kamu Malı
Bu plan CC0 lisansıyla yayınlanmıştır. İzin almadan kopyalayabilir, değiştirebilir, dağıtabilir ve herhangi bir amaçla kullanabilirsiniz.
Planı üzerinden ürün satın alarak Maker'ı destekleyin, böylece Maker Komisyonu Satıcılar tarafından belirlenen komisyonu kazanırlar veya bu Planın yeni bir versiyonunu oluşturun ve gelir paylaşımı için kendi Planınıza bağlantı olarak ekleyin.